General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 20.0 °C | 2.77 g/cm³ Show Material materials with Densidad of 2.77 g/cm³ | T4510 | EN 573-3 | Rod |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Dureza Brinell | 20.0 °C | 110.0 [-] Show Material materials with Dureza Brinell of 110.0 [-] | T4510 | EN 573-3 | Rod | |
20.0 °C | 110.0 - 138.0 [-] Show Material materials with Dureza Brinell of 110.0 - 138.0 [-] | T4510 | EN 573-3 | Rod | ||
20.0 °C | 138.0 [-] Show Material materials with Dureza Brinell of 138.0 [-] | T4510 | EN 573-3 | Rod | ||
Elongación | 20.0 °C | 7.0 % Show Material materials with Elongación of 7.0 % | T4510 | EN 573-3 | Rod | |
Módulo de cizallamiento | 20.0 °C | 27.0 - 28.0 GPa Show Material materials with Módulo de cizallamiento of 27.0 - 28.0 GPa | T4510 | EN 573-3 | Rod | |
Módulo elástico | 20.0 °C | 70.0 - 74.5 GPa Show Material materials with Módulo elástico of 70.0 - 74.5 GPa | T4510 | EN 573-3 | Rod | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Resistencia a la tracción | 20.0 °C | 360.0 MPa Show Material materials with Resistencia a la tracción of 360.0 MPa | T4510 | EN 573-3 | Rod |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Calor específico | 20.0 °C | 875.0 J/(kg·K) Show Material materials with Calor específico of 875.0 J/(kg·K) | T4510 | EN 573-3 | Rod | |
Coeficiente de dilatación térmica | 1.6e-05 - 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 2000 Series Aluminium | ||||
Conductividad térmica | 20.0 °C | 130.0 - 150.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 - 150.0 W/(m·K) | T4510 | EN 573-3 | Rod | |
Temperatura de fusión | 500.0 - 650.0 °C Show Material materials with Temperatura de fusión of 500.0 - 650.0 °C | Typical for Wrought 2000 Series Aluminium |
Eléctrico
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 18000000.0 - 21000000.0 S/m Show Material materials with Conductividad eléctrica of 18000000.0 - 21000000.0 S/m | T4510 | EN 573-3 | Rod | |
Resistividad eléctrica | 3.4e-08 - 6e-08 Ω·m Show Material materials with Resistividad eléctrica of 3.4e-08 - 6e-08 Ω·m | Typical for Wrought 2000 Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Cobre | 3.8 - 4.9 % Show Material materials with Cobre of 3.8 - 4.9 % | T4510 | EN 573-3 | Rod |
Cromo | 0.1 Show Material materials with Cromo of 0.1 | T4510 | EN 573-3 | Rod |
Hierro | 0.5 Show Material materials with Hierro of 0.5 | T4510 | EN 573-3 | Rod |
Magnesio | 1.2 - 1.8 % Show Material materials with Magnesio of 1.2 - 1.8 % | T4510 | EN 573-3 | Rod |
Manganeso | 0.3 - 0.9 % Show Material materials with Manganeso of 0.3 - 0.9 % | T4510 | EN 573-3 | Rod |
Silicona | 0.5 Show Material materials with Silicona of 0.5 | T4510 | EN 573-3 | Rod |
Titanio | 0.15 Show Material materials with Titanio of 0.15 | T4510 | EN 573-3 | Rod |
Zinc | 0.25 Show Material materials with Zinc of 0.25 | T4510 | EN 573-3 | Rod |
Technological properties
Property | ||
---|---|---|
Workability | Moderate Workability |