General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 20.0 °C | 4.45 g/cm³ Show Material materials with Densidad of 4.45 g/cm³ | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elongación | 20.0 °C | 6.0 % Show Material materials with Elongación of 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | |
Estricción | 20.0 °C | 15.0 % Show Material materials with Estricción of 15.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | |
Límite elástico | 20.0 °C | 880.0 MPa Show Material materials with Límite elástico of 880.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod | RP02 |
20.0 °C | 940.0 - 962.0 MPa Show Material materials with Límite elástico of 940.0 - 962.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 940.0 MPa Show Material materials with Límite elástico of 940.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 940.0 - 967.0 MPa Show Material materials with Límite elástico of 940.0 - 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 962.0 MPa Show Material materials with Límite elástico of 962.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 962.0 - 967.0 MPa Show Material materials with Límite elástico of 962.0 - 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 967.0 MPa Show Material materials with Límite elástico of 967.0 MPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
Módulo de cizallamiento | 20.0 °C | 47.0 GPa Show Material materials with Módulo de cizallamiento of 47.0 GPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Módulo elástico | 20.0 °C | 125.0 GPa Show Material materials with Módulo elástico of 125.0 GPa | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Plane-Strain Fracture Toughnes | 20.0 °C | 64.8 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | |
20.0 °C | 64.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 64.8 - 67.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 67.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 64.8 - 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 64.8 - 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 67.9 - 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 67.9 - 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 68.3 - 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 68.3 - 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 68.3 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 68.3 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
20.0 °C | 74.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 74.9 MPa·√m | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging | ||
Resistencia a la tracción | 20.0 °C | 950.0 MPa Show Material materials with Resistencia a la tracción of 950.0 MPa | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Calor específico | 20.0 °C | 540.0 J/(kg·K) Show Material materials with Calor específico of 540.0 J/(kg·K) | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Coeficiente de dilatación térmica | 7.099999999999997e-06 - 9.699999999999999e-06 1/K Show Material materials with Coeficiente de dilatación térmica of 7.099999999999997e-06 - 9.699999999999999e-06 1/K | Typical for Titanium Beta Alloy | ||||
Conductividad térmica | 20.0 °C | 4.2 W/(m·K) Show Material materials with Conductividad térmica of 4.2 W/(m·K) | Artificially Aged | WL 3.7154-1, DIN 17851, DIN 17864 | Forging, Rod | |
Temperatura de fusión | 1550.0 - 1815.0 °C Show Material materials with Temperatura de fusión of 1550.0 - 1815.0 °C | Typical for Titanium Beta Alloy |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminio | 5.7 - 6.3 % Show Material materials with Aluminio of 5.7 - 6.3 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Carbono | 0.08 Show Material materials with Carbono of 0.08 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging |
Circonio | 4.0 - 6.0 % Show Material materials with Circonio of 4.0 - 6.0 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Hidrógeno | 0.015 Show Material materials with Hidrógeno of 0.015 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging |
Hierro | 0.2 Show Material materials with Hierro of 0.2 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Molibdeno | 0.25 - 0.75 % Show Material materials with Molibdeno of 0.25 - 0.75 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Nitrógeno | 0.05 Show Material materials with Nitrógeno of 0.05 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Oxígeno | 0.19 Show Material materials with Oxígeno of 0.19 | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Silicona | 0.1 - 0.4 % Show Material materials with Silicona of 0.1 - 0.4 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |
Titanio | 85.6 % Show Material materials with Titanio of 85.6 % | Artificially Aged | DIN 17851, DIN 17864, WL 3.7154-1 | Forging, Rod |