DIN 17851 Grade TiAl6V6Sn2 Annealed

Want to keep this datasheet? Save it now in your required format

Description

Chemical composition: DIN 17851 TiAl6V6Sn2 with the material number 3.7175 (see also TiAl6V6Sn2, material number 3.7174, according to the Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL 3.7174) belongs to the hardenable alpha + beta-titanium alloys. It is similar to the 3.7164 or 3.7165 (TiAl6V4), yet the beta-phase is more stable and the material shows higher strength. It possesses good resistance to corrosion, it is well forgeable, and the long-term application temperature is approximately 350 °C. Processing properties: Formability: limited (cold forming), good (hot forming) Weldability: limited (embrittlement of the welding and heat affected zone by transformation hardening, electron-beam welding) (Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL: material specification of the German aviation)

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Condition	Related Standards	Shape
Densidad	20.0 °C	4.54 g/cm³ Show Material materials with Densidad of 4.54 g/cm³	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat

Mecánica

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Dureza Brinell	20.0 °C	320.0 Show Material materials with Dureza Brinell of 320.0	Annealed	DIN 17862, WL 3.7174-1, DIN 17851, DIN 17864, DIN 17860	Rod
Elongación	20.0 °C	6.0 % Show Material materials with Elongación of 6.0 %	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	7.0 % Show Material materials with Elongación of 7.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod	Transverse
	20.0 °C	8.0 % Show Material materials with Elongación of 8.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
Estricción	20.0 °C	15.0 % Show Material materials with Estricción of 15.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging	Transverse
	20.0 °C	20.0 % Show Material materials with Estricción of 20.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
Módulo de cizallamiento	20.0 °C	45.0 GPa Show Material materials with Módulo de cizallamiento of 45.0 GPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Forging, Plate, Rod, Flat
Módulo elástico	20.0 °C	116.0 GPa Show Material materials with Módulo elástico of 116.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
	200.0 °C	108.0 GPa Show Material materials with Módulo elástico of 108.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
	400.0 °C	99.0 GPa Show Material materials with Módulo elástico of 99.0 GPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Plane-Strain Fracture Toughnes	20.0 °C	46.1 - 54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 - 54.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	46.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.1 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	54.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 54.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	62.7 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	62.7 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	62.7 - 70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 62.7 - 70.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	70.8 - 71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 - 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	70.8 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 70.8 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
	20.0 °C	71.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 71.9 MPa·√m	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Rod, Forging
Resistencia a la tracción	20.0 °C	1000.0 MPa Show Material materials with Resistencia a la tracción of 1000.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod	Transverse
	20.0 °C	1000.0 MPa Show Material materials with Resistencia a la tracción of 1000.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate
	20.0 °C	1030.0 MPa Show Material materials with Resistencia a la tracción of 1030.0 MPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Plate
	20.0 °C	1070.0 MPa Show Material materials with Resistencia a la tracción of 1070.0 MPa	Annealed	WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Flat
	20.0 °C	1140.0 MPa Show Material materials with Resistencia a la tracción of 1140.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	100.0 °C	1065.0 MPa Show Material materials with Resistencia a la tracción of 1065.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	200.0 °C	990.0 MPa Show Material materials with Resistencia a la tracción of 990.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	300.0 °C	930.0 MPa Show Material materials with Resistencia a la tracción of 930.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860
	400.0 °C	900.0 MPa Show Material materials with Resistencia a la tracción of 900.0 MPa	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860

Aplicaciones térmicas

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Calor específico		370.0 - 674.0 J/(kg·K) Show Material materials with Calor específico of 370.0 - 674.0 J/(kg·K)				Typical for Titanium Alpha Beta Alloy
Coeficiente de dilatación térmica		7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 7.699999999999999e-06 - 1e-05 1/K				Typical for Titanium Alpha Beta Alloy
Conductividad térmica	20.0 °C	6.5 W/(m·K) Show Material materials with Conductividad térmica of 6.5 W/(m·K)	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Temperatura de fusión		1500.0 - 1750.0 °C Show Material materials with Temperatura de fusión of 1500.0 - 1750.0 °C				Typical for Titanium Alpha Beta Alloy

Eléctrico

Property	Temperature	Value	Condition	Related Standards	Shape
Resistividad eléctrica	20.0 °C	1.57e-06 Ω·m Show Material materials with Resistividad eléctrica of 1.57e-06 Ω·m	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat

Chemical properties

Property	Value	Condition	Related Standards	Shape
Aluminio	5.0 - 6.0 % Show Material materials with Aluminio of 5.0 - 6.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Carbono	0.05 Show Material materials with Carbono of 0.05	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Cobre	0.35 - 1.0 % Show Material materials with Cobre of 0.35 - 1.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Estaño	1.5 - 2.5 % Show Material materials with Estaño of 1.5 - 2.5 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Hidrógeno	0.015 Show Material materials with Hidrógeno of 0.015	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod
Hierro	0.35 - 1.0 % Show Material materials with Hierro of 0.35 - 1.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Nitrógeno	0.04 Show Material materials with Nitrógeno of 0.04	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Oxígeno	0.2 Show Material materials with Oxígeno of 0.2	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Titanio	82.8 % Show Material materials with Titanio of 82.8 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat
Vanadio	5.0 - 6.0 % Show Material materials with Vanadio of 5.0 - 6.0 %	Annealed	DIN 17851, DIN 17864, WL 3.7174-1, DIN 17862, DIN 17860	Forging, Rod, Plate, Flat