General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 20.0 °C | 2.75 g/cm³ Show Material materials with Densidad of 2.75 g/cm³ | T5 | DIN 1725-2, EN 1676, EN 1706 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 2xx.x Series Aluminium | |||
Dureza Brinell | 20.0 °C | 90.0 [-] Show Material materials with Dureza Brinell of 90.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 95.0 - 110.0 [-] Show Material materials with Dureza Brinell of 95.0 - 110.0 [-] | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Elongación | 20.0 °C | 2.0 % Show Material materials with Elongación of 2.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 3.0 % Show Material materials with Elongación of 3.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 3.0 - 8.0 % Show Material materials with Elongación of 3.0 - 8.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 7.0 - 12.0 % Show Material materials with Elongación of 7.0 - 12.0 % | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
Módulo elástico | 20.0 °C | 72.0 GPa Show Material materials with Módulo elástico of 72.0 GPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Resistencia a la tracción | 20.0 °C | 250.0 MPa Show Material materials with Resistencia a la tracción of 250.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | |
20.0 °C | 280.0 MPa Show Material materials with Resistencia a la tracción of 280.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 300.0 - 380.0 MPa Show Material materials with Resistencia a la tracción of 300.0 - 380.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 | ||
20.0 °C | 330.0 - 400.0 MPa Show Material materials with Resistencia a la tracción of 330.0 - 400.0 MPa | T5 | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 20.0 °C | 900.0 J/(kg·K) Show Material materials with Calor específico of 900.0 J/(kg·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 200.0 °C | 2.4e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.4e-05 1/K | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 20.0 °C | 110.0 - 140.0 W/(m·K) Show Material materials with Conductividad térmica of 110.0 - 140.0 W/(m·K) | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 510.0 - 790.0 °C Show Material materials with Temperatura de fusión of 510.0 - 790.0 °C | Typical for Cast 2xx.x Series Aluminium |
Eléctrico
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 16000000.0 - 20000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 20000000.0 S/m | T5 | DIN 1725-2, EN 1676, EN 1706 | |
Resistividad eléctrica | 4.347826086956522e-08 - 6.25e-08 Ω·m Show Material materials with Resistividad eléctrica of 4.347826086956522e-08 - 6.25e-08 Ω·m | Typical for Cast 2xx.x Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 93.5 % Show Material materials with Aluminio of 93.5 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Cobre | 4.5 - 5.2 % Show Material materials with Cobre of 4.5 - 5.2 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 0.18 Show Material materials with Hierro of 0.18 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.001 - 0.5 % Show Material materials with Manganeso of 0.001 - 0.5 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 0.18 Show Material materials with Silicona of 0.18 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.15 - 0.3 % Show Material materials with Titanio of 0.15 - 0.3 % | T5 | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.07 Show Material materials with Zinc of 0.07 | T5 | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Processing methods | permanent mould casting, sample taken from casting |