General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 20.0 °C | 2.65 g/cm³ Show Material materials with Densidad of 2.65 g/cm³ | F | DIN 1725-2, EN 1676, EN 1706 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Dureza Brinell | 20.0 °C | 70.0 - 100.0 [-] Show Material materials with Dureza Brinell of 70.0 - 100.0 [-] | F | DIN 1725-2, EN 1676, EN 1706 | |
Elongación | 20.0 °C | 1.0 - 3.0 % Show Material materials with Elongación of 1.0 - 3.0 % | F | DIN 1725-2, EN 1676, EN 1706 | |
Módulo de cizallamiento | 2.8 GPa Show Material materials with Módulo de cizallamiento of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Módulo elástico | 20.0 °C | 74.0 GPa Show Material materials with Módulo elástico of 74.0 GPa | F | DIN 1725-2, EN 1676, EN 1706 | |
Resistencia a la tracción | 20.0 °C | 220.0 - 300.0 MPa Show Material materials with Resistencia a la tracción of 220.0 - 300.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 | |
Resistencia al cizallamiento | 20.0 °C | 147.0 MPa Show Material materials with Resistencia al cizallamiento of 147.0 MPa | F | DIN 1725-2, EN 1676, EN 1706 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Calor específico | 20.0 °C | 910.0 J/(kg·K) Show Material materials with Calor específico of 910.0 J/(kg·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Coeficiente de dilatación térmica | 200.0 °C | 2.1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 2.1e-05 1/K | F | DIN 1725-2, EN 1676, EN 1706 | |
Conductividad térmica | 20.0 °C | 120.0 - 150.0 W/(m·K) Show Material materials with Conductividad térmica of 120.0 - 150.0 W/(m·K) | F | DIN 1725-2, EN 1676, EN 1706 | |
Temperatura de fusión | 505.0 - 770.0 °C Show Material materials with Temperatura de fusión of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Eléctrico
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Conductividad eléctrica | 20.0 °C | 16000000.0 - 20000000.0 S/m Show Material materials with Conductividad eléctrica of 16000000.0 - 20000000.0 S/m | F | DIN 1725-2, EN 1676, EN 1706 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminio | 86.6 % Show Material materials with Aluminio of 86.6 % | F | DIN 1725-2, EN 1676, EN 1706 |
Cobre | 0.1 Show Material materials with Cobre of 0.1 | F | DIN 1725-2, EN 1676, EN 1706 |
Hierro | 1.0 Show Material materials with Hierro of 1.0 | F | DIN 1725-2, EN 1676, EN 1706 |
Magnesio | 0.2 - 0.5 % Show Material materials with Magnesio of 0.2 - 0.5 % | F | DIN 1725-2, EN 1676, EN 1706 |
Manganeso | 0.001 - 0.4 % Show Material materials with Manganeso of 0.001 - 0.4 % | F | DIN 1725-2, EN 1676, EN 1706 |
Silicona | 9.0 - 11.0 % Show Material materials with Silicona of 9.0 - 11.0 % | F | DIN 1725-2, EN 1676, EN 1706 |
Titanio | 0.15 Show Material materials with Titanio of 0.15 | F | DIN 1725-2, EN 1676, EN 1706 |
Zinc | 0.1 Show Material materials with Zinc of 0.1 | F | DIN 1725-2, EN 1676, EN 1706 |
Technological properties
Property | ||
---|---|---|
Processing methods | pressure die casting, separately cast test sample |