Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 20 g/cm³ Show Material materials with Densidad of 20 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.39 [-] Show Material materials with Coeficiente de Poisson of 0.39 [-] | Typical for Platinum |
Dureza Vickers | 20.0 °C | 204 [-] Show Material materials with Dureza Vickers of 204 [-] | |
Elongación | 20.0 °C | 2 % Show Material materials with Elongación of 2 % | |
Límite elástico Rp 0,2 | 20.0 °C | 670 MPa Show Material materials with Límite elástico Rp 0,2 of 670 MPa | |
Módulo de cizallamiento | 20.0 °C | 72 GPa Show Material materials with Módulo de cizallamiento of 72 GPa | |
Módulo elástico | 20.0 °C | 208 GPa Show Material materials with Módulo elástico of 208 GPa | |
Resistencia a la tracción | 20.0 °C | 660 MPa Show Material materials with Resistencia a la tracción of 660 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 136 J/(kg·K) Show Material materials with Calor específico of 136 J/(kg·K) | Typical for Platinum |
Coeficiente de dilatación térmica | 300.0 °C | 1.02E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.02E-5 1/K | |
700.0 °C | 1.07E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.07E-5 1/K | ||
1200.0 °C | 1.12E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.12E-5 1/K | ||
Conductividad térmica | 20.0 °C | 30 W/(m·K) Show Material materials with Conductividad térmica of 30 W/(m·K) | |
Temperatura de fusión | 1769 °C Show Material materials with Temperatura de fusión of 1769 °C | Typical for Platinum |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 20.0 °C | 2.06E-7 Ω·m Show Material materials with Resistividad eléctrica of 2.06E-7 Ω·m |
Chemical properties