General
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Densidad | 20.0 °C | 2.7 g/cm³ Show Material materials with Densidad of 2.7 g/cm³ | H3x | WL 3.2134 |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Material materials with Coeficiente de Poisson of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | |||
Dureza Brinell | 20.0 °C | 60.0 [-] Show Material materials with Dureza Brinell of 60.0 [-] | H3x | WL 3.2134 | |
20.0 °C | 65.0 [-] Show Material materials with Dureza Brinell of 65.0 [-] | H3x | WL 3.2134 | ||
20.0 °C | 70.0 [-] Show Material materials with Dureza Brinell of 70.0 [-] | H3x | WL 3.2134 | ||
Elongación | 20.0 °C | 0.5 % Show Material materials with Elongación of 0.5 % | H3x | WL 3.2134 | |
20.0 °C | 1.0 % Show Material materials with Elongación of 1.0 % | H3x | WL 3.2134 | ||
20.0 °C | 1.5 % Show Material materials with Elongación of 1.5 % | H3x | WL 3.2134 | ||
20.0 °C | 2.0 % Show Material materials with Elongación of 2.0 % | H3x | WL 3.2134 | ||
Módulo de cizallamiento | 2.8 GPa Show Material materials with Módulo de cizallamiento of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | |||
Módulo elástico | 20.0 °C | 71.0 GPa Show Material materials with Módulo elástico of 71.0 GPa | H3x | WL 3.2134 | |
Resistencia a la tracción | 20.0 °C | 150.0 MPa Show Material materials with Resistencia a la tracción of 150.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa Show Material materials with Resistencia a la tracción of 160.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 180.0 MPa Show Material materials with Resistencia a la tracción of 180.0 MPa | H3x | WL 3.2134 | ||
20.0 °C | 190.0 MPa Show Material materials with Resistencia a la tracción of 190.0 MPa | H3x | WL 3.2134 | ||
Resistencia al cizallamiento | 20.0 °C | 120.0 MPa Show Material materials with Resistencia al cizallamiento of 120.0 MPa | H3x | WL 3.2134 | |
20.0 °C | 160.0 MPa Show Material materials with Resistencia al cizallamiento of 160.0 MPa | H3x | WL 3.2134 |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Calor específico | 960.0 - 963.0 J/(kg·K) Show Material materials with Calor específico of 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium |
Coeficiente de dilatación térmica | 1.6e-05 - 2.3e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6e-05 - 2.3e-05 1/K | Typical for Cast 3xx.x Series Aluminium |
Conductividad térmica | 130.0 - 180.0 W/(m·K) Show Material materials with Conductividad térmica of 130.0 - 180.0 W/(m·K) | Typical for Cast 3xx.x Series Aluminium |
Temperatura de fusión | 505.0 - 770.0 °C Show Material materials with Temperatura de fusión of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Cobre | 1.0 - 1.5 % Show Material materials with Cobre of 1.0 - 1.5 % | H3x | WL 3.2134 |
Cromo | 0.25 Show Material materials with Cromo of 0.25 | H3x | WL 3.2134 |
Hierro | 0.6 Show Material materials with Hierro of 0.6 | H3x | WL 3.2134 |
Magnesio | 0.4 - 0.6 % Show Material materials with Magnesio of 0.4 - 0.6 % | H3x | WL 3.2134 |
Manganeso | 0.5 Show Material materials with Manganeso of 0.5 | H3x | WL 3.2134 |
Silicona | 4.5 - 5.5 % Show Material materials with Silicona of 4.5 - 5.5 % | H3x | WL 3.2134 |
Titanio | 0.25 Show Material materials with Titanio of 0.25 | H3x | WL 3.2134 |
Zinc | 0.3 Show Material materials with Zinc of 0.3 | H3x | WL 3.2134 |
Technological properties
Property | ||
---|---|---|
Processing methods | permanent mould casting |