Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 100.0 °C | 963 J/(kg·K) Show Material materials with Calor específico of 963 J/(kg·K) |
Coeficiente de dilatación térmica | 100.0 °C | 2.16E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.16E-5 1/K |
Conductividad térmica | 20.0 °C | 150 W/(m·K) Show Material materials with Conductividad térmica of 150 W/(m·K) |
Temperatura de fusión | 610 °C Show Material materials with Temperatura de fusión of 610 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 20.0 °C | 2.00E+7 - 2.30E+7 S/m Show Material materials with Conductividad eléctrica of 2.00E+7 - 2.30E+7 S/m |
General
Property | Temperature | Value |
---|---|---|
Densidad | 20.0 °C | 2.68 g/cm³ Show Material materials with Densidad of 2.68 g/cm³ |
Mecánica
Property | Temperature | Value |
---|---|---|
Elongación | 20.0 °C | 2 - 5 % Show Material materials with Elongación of 2 - 5 % |
Límite elástico Rp 0,2 | 20.0 °C | 220 - 275 MPa Show Material materials with Límite elástico Rp 0,2 of 220 - 275 MPa |
Módulo elástico | 20.0 °C | 71.5 GPa Show Material materials with Módulo elástico of 71.5 GPa |
Resistencia a la fractura | 20.0 °C | 22 MPa·√m Show Material materials with Resistencia a la fractura of 22 MPa·√m |
Resistencia a la tracción | 20.0 °C | 280 - 345 MPa Show Material materials with Resistencia a la tracción of 280 - 345 MPa |
Chemical properties
Property | Value |
---|---|
Berilio | 0.07 % Show Material materials with Berilio of 0.07 % |
Cobre | 0.2 % Show Material materials with Cobre of 0.2 % |
Hierro | 0.2 % Show Material materials with Hierro of 0.2 % |
Magnesio | 0.45 - 0.7 % Show Material materials with Magnesio of 0.45 - 0.7 % |
Manganeso | 0.1 % Show Material materials with Manganeso of 0.1 % |
Silicona | 6.5 - 7.5 % Show Material materials with Silicona of 6.5 - 7.5 % |
Titanio | 0.1 - 0.2 % Show Material materials with Titanio of 0.1 - 0.2 % |
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % |