General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.22 g/cm³ Show Material materials with Density of 8.22 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Elastic modulus | 23.0 °C | 204 GPa Show Material materials with Elastic modulus of 204 GPa |
Elongation | 23.0 °C | 12 - 17 % Show Material materials with Elongation of 12 - 17 % |
Hardness, Brinell | 23.0 °C | 313 - 354 [-] Show Material materials with Hardness, Brinell of 313 - 354 [-] |
Reduction of area | 23.0 °C | 15 % Show Material materials with Reduction of area of 15 % |
Tensile strength | 23.0 °C | 1034 - 1276 MPa Show Material materials with Tensile strength of 1034 - 1276 MPa |
Yield strength Rp0.2 | 23.0 °C | 827 - 1034 MPa Show Material materials with Yield strength Rp0.2 of 827 - 1034 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.35E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.35E-5 1/K | |
Melting point | 1260 - 1335 °C Show Material materials with Melting point of 1260 - 1335 °C | ||
Thermal conductivity | 23.0 °C | 14.2 W/(m·K) Show Material materials with Thermal conductivity of 14.2 W/(m·K) | for 0-200°C |
Magnetic
Property | Temperature | Value |
---|---|---|
Relative magnetic permeability | 23.0 °C | 1 [-] Show Material materials with Relative magnetic permeability of 1 [-] |
Chemical properties
Property | Value |
---|---|
Aluminium | 0.5 % Show Material materials with Aluminium of 0.5 % |
Chromium | 19 % Show Material materials with Chromium of 19 % |
Iron | 18 - 18.5 % Show Material materials with Iron of 18 - 18.5 % |
Molybdenum | 3 % Show Material materials with Molybdenum of 3 % |
Nickel | 53 % Show Material materials with Nickel of 53 % |
Niobium | 5 % Show Material materials with Niobium of 5 % |
Titanium | 0.9 % Show Material materials with Titanium of 0.9 % |
Technological properties
Property | ||
---|---|---|
Application areas | Offshore & marine: Fasteners, valves, choke stems, down-hole tooling, cryogenic storage tanks and pump bodies;Aerospace: Jet engine components, rocket motors and thrust reversers;Power generation: Nuclear reactor parts, gas turbine components, nuclear fuel element spacers, containment vessels and valves;Other: Hot extrusion tooling | |
Corrosion properties | Excellent corrosion resistance | |
Hot forming | It can be hot worked between 985-1150°C. |