Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 6.05 g/cm³ Show Supplier Material materials with Dichte of 6.05 g/cm³ | |
Oberflächenrauigkeit | 3.6 μm Show Supplier Material materials with Oberflächenrauigkeit of 3.6 μm | Rz* |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 1100 MPa Show Supplier Material materials with Biegefestigkeit of 1100 MPa | 4-point bending flexural test |
Druckfestigkeit | 23.0 °C | 2400 MPa Show Supplier Material materials with Druckfestigkeit of 2400 MPa | |
Elastizitätsmodul | 23.0 °C | 210 GPa Show Supplier Material materials with Elastizitätsmodul of 210 GPa | |
Härte, Vickers | 23.0 °C | 1326 [-] Show Supplier Material materials with Härte, Vickers of 1326 [-] | converted from GPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 10.5 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10.5 MPa·√m |
Thermisch
Elektrisch
Property | Temperature | Value |
---|---|---|
spezifischer Widerstand | 20.0 °C | 1.00E+9 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.00E+9 Ω·m |
600.0 °C | 10000 Ω·m Show Supplier Material materials with spezifischer Widerstand of 10000 Ω·m | |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor Technology (lambda sensors) for oxygen ion conduction Components that face frequent temperature changes, e.g. draw dies and high-temperature insulating parts In cases where high fracture toughness is required, e.g. for medical instruments | |
Other | *depending on the processing status of the injection molding or pressing tool | |
Processing history | Ceramic Injection Molding (CIM) |