Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 6.05 g/cm³ Show Supplier Material materials with Dichte of 6.05 g/cm³ | |
Oberflächenrauigkeit | 0.6 μm Show Supplier Material materials with Oberflächenrauigkeit of 0.6 μm | Ra |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 930 MPa Show Supplier Material materials with Biegefestigkeit of 930 MPa | 4-point bending flexural test |
Druckfestigkeit | 23.0 °C | 2300 MPa Show Supplier Material materials with Druckfestigkeit of 2300 MPa | |
Elastizitätsmodul | 23.0 °C | 205 GPa Show Supplier Material materials with Elastizitätsmodul of 205 GPa | |
Härte, Vickers | 23.0 °C | 1530 [-] Show Supplier Material materials with Härte, Vickers of 1530 [-] | converted from GPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 10 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10 MPa·√m |
Thermisch
Elektrisch
Property | Temperature | Value |
---|---|---|
spezifischer Widerstand | 20.0 °C | 1.00E+10 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1.00E+10 Ω·m |
600.0 °C | 10000 Ω·m Show Supplier Material materials with spezifischer Widerstand of 10000 Ω·m | |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor Technology (lambda sensors) for oxygen ion conduction Components that face frequent temperature changes, e.g. draw dies and high-temperature insulating parts In cases where high fracture toughness is required, e.g. for medical instruments | |
Processing history | Additive Manufactureing (AM) |