Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 8.43 g/cm³ Show Supplier Material materials with Dichte of 8.43 g/cm³ | |
Korngröße | 4 μm Show Supplier Material materials with Korngröße of 4 μm | Maximum, ASTM E112 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 8 % Show Supplier Material materials with Dehnung of 8 % | ASTM E8, For 50.8mm diameter |
Flächenreduzierung | 23.0 °C | 35 % Show Supplier Material materials with Flächenreduzierung of 35 % | ASTM E8, For 50.8mm diameter |
Härte, Rockwell C | 23.0 °C | 44 [-] Show Supplier Material materials with Härte, Rockwell C of 44 [-] | ASTM E18 |
Scherfestigkeit | 23.0 °C | 1034 MPa Show Supplier Material materials with Scherfestigkeit of 1034 MPa | For 25.4mm diameter |
Streckgrenze Rp 0,2 | 23.0 °C | 230 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 230 MPa | ASTM E8, For 50.8mm diameter |
Zugfestigkeit | 23.0 °C | 260 MPa Show Supplier Material materials with Zugfestigkeit of 260 MPa | ASTM E8, For 50.8mm diameter |
Chemical properties
Property | Value |
---|---|
Bor | 0.15 % Show Supplier Material materials with Bor of 0.15 % |
Chrom | 19 - 21 % Show Supplier Material materials with Chrom of 19 - 21 % |
Eisen | 1 % Show Supplier Material materials with Eisen of 1 % |
Kobalt | Balance |
Kohlenstoff | 0.025 % Show Supplier Material materials with Kohlenstoff of 0.025 % |
Mangan | 0.15 % Show Supplier Material materials with Mangan of 0.15 % |
Molybdän | 9 - 10.5 % Show Supplier Material materials with Molybdän of 9 - 10.5 % |
Nickel | 33 - 37 % Show Supplier Material materials with Nickel of 33 - 37 % |
Phosphor | 0.02 % Show Supplier Material materials with Phosphor of 0.02 % |
Schwefel | 0.01 % Show Supplier Material materials with Schwefel of 0.01 % |
Silizium | 0.15 % Show Supplier Material materials with Silizium of 0.15 % |
Titan | 1 % Show Supplier Material materials with Titan of 1 % |
Technological properties
Property | ||
---|---|---|
Application areas | The high strength variant of MP35N™ is used in a wide range of applications, in aerospace particularly for fasteners and airframe components. Elsewhere MP35N is used in motor sports, medical etc. for fasteners, springs, non-magnetic electrical components, instrument parts, valve components, high pressure door fittings, actuators, seals, shafts and other components. | |
Corrosion properties | This material has generally excellent corrosion resistance properties, including stress corrosion cracking (SCC) resistance for harsh environments as well as resists attack from mineral acids (nitric, hydrochloric and sulphur). The material also has exceptional resistance to crevice and stress corrosion cracking in hostile environments. |