Eigenschaften
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Dehnung | 23.0 °C | 25 % Show Supplier Material materials with Dehnung of 25 % |
Härte, HBW | 23.0 °C | 290 [-] Show Supplier Material materials with Härte, HBW of 290 [-] |
Härte, Rockwell C | 23.0 °C | 31 [-] Show Supplier Material materials with Härte, Rockwell C of 31 [-] |
Zugfestigkeit | 23.0 °C | 750 MPa Show Supplier Material materials with Zugfestigkeit of 750 MPa |
Chemical properties
| Property | Value |
|---|---|
Chrom | 24 - 26 % Show Supplier Material materials with Chrom of 24 - 26 % |
Eisen | Balance |
Kohlenstoff | 0.03 % Show Supplier Material materials with Kohlenstoff of 0.03 % |
Kupfer | 0.5 - 1 % Show Supplier Material materials with Kupfer of 0.5 - 1 % |
Mangan | 1 % Show Supplier Material materials with Mangan of 1 % |
Molybdän | 3 - 4 % Show Supplier Material materials with Molybdän of 3 - 4 % |
Nickel | 6 - 8 % Show Supplier Material materials with Nickel of 6 - 8 % |
Phosphor | 0.03 % Show Supplier Material materials with Phosphor of 0.03 % |
Schwefel | 0.01 % Show Supplier Material materials with Schwefel of 0.01 % |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % |
Stickstoff | 0.2 - 0.3 % Show Supplier Material materials with Stickstoff of 0.2 - 0.3 % |
Wolfram | 0.5 - 1 % Show Supplier Material materials with Wolfram of 0.5 - 1 % |
Technological properties
| Property | ||
|---|---|---|
| Corrosion properties | Stress Corrosion: material is tested in accordance with ASTM G48 (Method A) (latest version). The test piece will be taken from the same location as those for mechanical testing. Acceptance is that no pitting is to be observed at 20x magnification after exposure for 24 hours at 50 degrees C. Weight loss will not exceed 4.0 g/mm2. Method and results are reported. | |