Beschreibung

Supplied in solution-annealed condition. Ferro-Titanit® Cromoni is non-magnetisable, even after ageing at temperatures up to 900 °C.

Ashby charts

See where falls on the material property chart for Density against Elastic modulus in your materials selection and design process.

Eigenschaften

Allgemein

Density ρ

7.4 g/cm³ at 20 °C

Grain structure

Titanium carbide + austenite

Mechanisch

Compressive strength Rmc

1500 MPa at 20 °C

Elastic modulus E

277 GPa at 20 °C

Flexural strength σbend

1300 MPa at 20 °C

Hardness, Rockwell C HRC

54 [-] at 20 °C

Thermisch

Coefficient of thermal expansion α

9E-6 1/K at 100 °C

for 20°C to the mentioned temperature

Grafik verstecken

Thermal conductivity λ

12.4 W/(m·K) at 20 °C

Elektrisch

Electrical resistivity ρel

1.53E-6 Ω·m at 20 °C

Magnetisch

Relative magnetic permeability μrel

1.01 [-] at 20 °C

max.

Chemische Eigenschaften

Element

Gew. %

Kommentar

Ni

-

Balance

Other

22 %

TiC

Cr

20 %

Mo

15.5 %

Technische Eigenschaften

Application areas

This austenitic grade is used for applications requiring complete non-magnetisability, a high wear resistance and maximum corrosion resistance.

Corrosion properties

Besides having a high wear resistance, this alloy is extremely resistant to corrosion and scaling, as well as highly tempering-resistant. This corrosion resistance is at its best with finely ground or polished surfaces.

General machinability

In as-delivered condition, this material can be machined by conventional methods.

Heat Treatment

Solution Anealing: 1200°C, 2 hr in vacuum (Cooling 4 bar N2) Hardness: 52 HRC - Age-Hardening 800°C, 6 hr in Vacuum, Hardness: 54 HRC

Diese Materialdaten wurden von Deutsche Edelstahlwerke Specialty Steel (DEW) zur Verfügung gestellt