Allgemein
Property | Value |
---|---|
Dichte | 8 g/cm³ Show Supplier Material materials with Dichte of 8 g/cm³ |
Abmessung
Property | Value | Comment |
---|---|---|
Durchmesser | 250 mm Show Supplier Material materials with Durchmesser of 250 mm | max. |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 100 J Show Supplier Material materials with Charpy impact energy, V-notch of 100 J | ||
Dehnung | 30 % Show Supplier Material materials with Dehnung of 30 % | A5 | Transverse | |
40 % Show Supplier Material materials with Dehnung of 40 % | A5 | ||
Elastizitätsmodul | 20 °C | 200 GPa Show Supplier Material materials with Elastizitätsmodul of 200 GPa | |
100 °C | 194 GPa Show Supplier Material materials with Elastizitätsmodul of 194 GPa | ||
200 °C | 186 GPa Show Supplier Material materials with Elastizitätsmodul of 186 GPa | ||
300 °C | 179 GPa Show Supplier Material materials with Elastizitätsmodul of 179 GPa | ||
400 °C | 172 GPa Show Supplier Material materials with Elastizitätsmodul of 172 GPa | ||
500 °C | 165 GPa Show Supplier Material materials with Elastizitätsmodul of 165 GPa | ||
Härte, Brinell | 215 [-] Show Supplier Material materials with Härte, Brinell of 215 [-] | ||
Härte, Rockwell C | 22 [-] Show Supplier Material materials with Härte, Rockwell C of 22 [-] | ||
Streckgrenze | 20 °C | 200 MPa Show Supplier Material materials with Streckgrenze of 200 MPa | RP02 |
23 °C | 235 MPa Show Supplier Material materials with Streckgrenze of 235 MPa | RP1 | |
100 °C | 165 MPa Show Supplier Material materials with Streckgrenze of 165 MPa | RP02 | |
100 °C | 200 MPa Show Supplier Material materials with Streckgrenze of 200 MPa | RP1 | |
150 °C | 150 MPa Show Supplier Material materials with Streckgrenze of 150 MPa | RP02 | |
150 °C | 180 MPa Show Supplier Material materials with Streckgrenze of 180 MPa | RP1 | |
200 °C | 137 MPa Show Supplier Material materials with Streckgrenze of 137 MPa | RP02 | |
200 °C | 165 MPa Show Supplier Material materials with Streckgrenze of 165 MPa | RP1 | |
250 °C | 127 MPa Show Supplier Material materials with Streckgrenze of 127 MPa | RP02 | |
250 °C | 153 MPa Show Supplier Material materials with Streckgrenze of 153 MPa | RP1 | |
300 °C | 119 MPa Show Supplier Material materials with Streckgrenze of 119 MPa | RP02 | |
300 °C | 145 MPa Show Supplier Material materials with Streckgrenze of 145 MPa | RP1 | |
350 °C | 113 MPa Show Supplier Material materials with Streckgrenze of 113 MPa | RP02 | |
350 °C | 139 MPa Show Supplier Material materials with Streckgrenze of 139 MPa | RP1 | |
400 °C | 108 MPa Show Supplier Material materials with Streckgrenze of 108 MPa | RP02 | |
400 °C | 135 MPa Show Supplier Material materials with Streckgrenze of 135 MPa | RP1 | |
450 °C | 103 MPa Show Supplier Material materials with Streckgrenze of 103 MPa | RP02 | |
450 °C | 130 MPa Show Supplier Material materials with Streckgrenze of 130 MPa | RP1 | |
500 °C | 100 MPa Show Supplier Material materials with Streckgrenze of 100 MPa | RP02 | |
500 °C | 128 MPa Show Supplier Material materials with Streckgrenze of 128 MPa | RP1 | |
550 °C | 98 MPa Show Supplier Material materials with Streckgrenze of 98 MPa | RP02 | |
550 °C | 127 MPa Show Supplier Material materials with Streckgrenze of 127 MPa | RP1 | |
Zugfestigkeit | 500 - 700 MPa Show Supplier Material materials with Zugfestigkeit of 500 - 700 MPa |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Koeffizient der thermischen Ausdehnung | 100 °C | 1.6e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.65e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.65e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.7e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.7e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.75e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.75e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.8e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.8e-05 1/K | for 20°C to the mentioned temperature | |
Spezifische Wärmekapazität | 500 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 500 J/(kg·K) | ||
Wärmeleitfähigkeit | 15 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 15 W/(m·K) |
Elektrisch
Property | Value |
---|---|
spezifischer Widerstand | 7.5e-07 Ω·m Show Supplier Material materials with spezifischer Widerstand of 7.5e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Chrom | 16.5 - 18.5 % Show Supplier Material materials with Chrom of 16.5 - 18.5 % |
Eisen | Balance |
Kohlenstoff | 0.03 % Show Supplier Material materials with Kohlenstoff of 0.03 % |
Mangan | 2 % Show Supplier Material materials with Mangan of 2 % |
Molybdän | 2 - 2.5 % Show Supplier Material materials with Molybdän of 2 - 2.5 % |
Nickel | 10 - 13 % Show Supplier Material materials with Nickel of 10 - 13 % |
Phosphor | 0.045 % Show Supplier Material materials with Phosphor of 0.045 % |
Schwefel | 0.03 % Show Supplier Material materials with Schwefel of 0.03 % |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % |
Stickstoff | 0.1 % Show Supplier Material materials with Stickstoff of 0.1 % |
Technological properties
Property | ||
---|---|---|
Application areas | Chemical Industry, Pharmaceutical Industry, Food Industry, Fittings, Construction, Ship Building & Marine Structures, Petrochemistry, Automotive, Decorative Applications, Kitchen Equipment, Electronics, Aerospace, Maritime | |
Cold Forming | It is suitable for cold forming according to DIN EN 10263-5. | |
Corrosion properties | Due to the molybdenum content has a higher corrosion resistance thatn Acidur 4301 and 4307 (specially in chloride mediums). Due to its low carbon content it is resistant against intergranular corrosion according to DIN EN 3651 part 2. PREN= 23.1-28.8 | |
Heat Treatment | Solution annealing: 1020-1120°C (water, air) fast cooling | |
Hot forming | It is formable at 900-1200°C | |
Processing history | Solution Annealed | |
Welding | It is weldable with or without filler material (e.g. 1.4430). The interpass temperature should not exceed 200°C. Subsequent heat treatment is not require. The resistance to intergranular corrosion is not affected by welding according to DIN EN 3651 part 2. |