Allgemein
Property | Value |
---|---|
Dichte | 7.9 g/cm³ Show Supplier Material materials with Dichte of 7.9 g/cm³ |
Abmessung
Property | Value | Comment |
---|---|---|
Durchmesser | 250 mm Show Supplier Material materials with Durchmesser of 250 mm | max. |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 100 J Show Supplier Material materials with Charpy impact energy, V-notch of 100 J | ||
Dehnung | 35 % Show Supplier Material materials with Dehnung of 35 % | A5 | Transverse | |
45 % Show Supplier Material materials with Dehnung of 45 % | A5 | ||
Elastizitätsmodul | 20 °C | 200 GPa Show Supplier Material materials with Elastizitätsmodul of 200 GPa | |
100 °C | 194 GPa Show Supplier Material materials with Elastizitätsmodul of 194 GPa | ||
200 °C | 186 GPa Show Supplier Material materials with Elastizitätsmodul of 186 GPa | ||
300 °C | 179 GPa Show Supplier Material materials with Elastizitätsmodul of 179 GPa | ||
400 °C | 172 GPa Show Supplier Material materials with Elastizitätsmodul of 172 GPa | ||
500 °C | 165 GPa Show Supplier Material materials with Elastizitätsmodul of 165 GPa | ||
Härte, Brinell | 215 [-] Show Supplier Material materials with Härte, Brinell of 215 [-] | ||
Streckgrenze | 20 °C | 190 MPa Show Supplier Material materials with Streckgrenze of 190 MPa | RP02 |
23 °C | 225 MPa Show Supplier Material materials with Streckgrenze of 225 MPa | RP1 | |
100 °C | 155 MPa Show Supplier Material materials with Streckgrenze of 155 MPa | RP02 | |
100 °C | 190 MPa Show Supplier Material materials with Streckgrenze of 190 MPa | RP1 | |
150 °C | 140 MPa Show Supplier Material materials with Streckgrenze of 140 MPa | RP02 | |
150 °C | 170 MPa Show Supplier Material materials with Streckgrenze of 170 MPa | RP1 | |
200 °C | 127 MPa Show Supplier Material materials with Streckgrenze of 127 MPa | RP02 | |
200 °C | 155 MPa Show Supplier Material materials with Streckgrenze of 155 MPa | RP1 | |
250 °C | 118 MPa Show Supplier Material materials with Streckgrenze of 118 MPa | RP02 | |
250 °C | 145 MPa Show Supplier Material materials with Streckgrenze of 145 MPa | RP1 | |
300 °C | 110 MPa Show Supplier Material materials with Streckgrenze of 110 MPa | RP02 | |
300 °C | 135 MPa Show Supplier Material materials with Streckgrenze of 135 MPa | RP1 | |
350 °C | 104 MPa Show Supplier Material materials with Streckgrenze of 104 MPa | RP02 | |
350 °C | 129 MPa Show Supplier Material materials with Streckgrenze of 129 MPa | RP1 | |
400 °C | 98 MPa Show Supplier Material materials with Streckgrenze of 98 MPa | RP02 | |
400 °C | 125 MPa Show Supplier Material materials with Streckgrenze of 125 MPa | RP1 | |
450 °C | 95 MPa Show Supplier Material materials with Streckgrenze of 95 MPa | RP02 | |
450 °C | 122 MPa Show Supplier Material materials with Streckgrenze of 122 MPa | RP1 | |
500 °C | 95 MPa Show Supplier Material materials with Streckgrenze of 95 MPa | RP02 | |
500 °C | 120 MPa Show Supplier Material materials with Streckgrenze of 120 MPa | RP1 | |
550 °C | 90 MPa Show Supplier Material materials with Streckgrenze of 90 MPa | RP02 | |
550 °C | 120 MPa Show Supplier Material materials with Streckgrenze of 120 MPa | RP1 | |
Zugfestigkeit | 500 - 700 MPa Show Supplier Material materials with Zugfestigkeit of 500 - 700 MPa |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Koeffizient der thermischen Ausdehnung | 100 °C | 1.6e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.6e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.65e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.65e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.7e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.7e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.75e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.75e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.8e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.8e-05 1/K | for 20°C to the mentioned temperature | |
Spezifische Wärmekapazität | 500 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 500 J/(kg·K) | ||
Wärmeleitfähigkeit | 15 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 15 W/(m·K) |
Elektrisch
Property | Value |
---|---|
spezifischer Widerstand | 7.3e-07 Ω·m Show Supplier Material materials with spezifischer Widerstand of 7.3e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Chrom | 17.5 - 19.5 % Show Supplier Material materials with Chrom of 17.5 - 19.5 % |
Eisen | Balance |
Kohlenstoff | 0.07 % Show Supplier Material materials with Kohlenstoff of 0.07 % |
Mangan | 2 % Show Supplier Material materials with Mangan of 2 % |
Nickel | 8 - 10.5 % Show Supplier Material materials with Nickel of 8 - 10.5 % |
Phosphor | 0.045 % Show Supplier Material materials with Phosphor of 0.045 % |
Schwefel | 0.03 % Show Supplier Material materials with Schwefel of 0.03 % |
Silizium | 1 % Show Supplier Material materials with Silizium of 1 % |
Stickstoff | 0.1 % Show Supplier Material materials with Stickstoff of 0.1 % |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive industry, Building and Construction industry, Chemical industry, Food and Beverage industry, Decorative items and Kitchen Utensils, Electronic Equipment, Petrochemical industry | |
Corrosion properties | Good - Due to the moderate carbon content of 1.4301, this grade of stainless steel is prone to sensitisation. The formation of chromium carbides and the associated chromium depleted regions that form around these precipitates make this grade of steel susceptible to intergranular corrosion. Although no danger of intergranular corrosion exists in the supplied (solution annealed) condition, intergranular corrosion may occur after welding or high temperature processing. 1.4301 is resistant to corrosion in most environments provided the chloride and salt concentrations are low. 1.4301 is not recommended for applications where it comes into contact with sea water, nor is it recommended for use in swimming pools. PRE = 17.5 – 21.36 | |
General machinability | Average - For applications which require machining, the NIRO-CUT® 4301 grade is recommended since the composition and production route followed to produce this grade compensates for the work hardening tendency of the material. | |
Heat Treatment | Optimal material properties are realised after solution annealing in the temperature range 1000 °C – 1100 °C followed by rapid cooling in air or water. Since this grade of steel is susceptible to precipitation of chromium carbides, care must be taken to limit the time spent in the temperature range 450 °C to 850 °C, both during fabrication and service. | |
Hot forming | It is formable at 900-1200°C | |
Processing history | Solution Annealed | |
Welding | Excellent - 1.4301 is weldable with or without the use of filler material. If the use of a filler metal is required, then the use of Novonit® 4316 (AISI 308L) would be recommended. Maximum interpass temperature 200 °C. Post weld heat treatment is not necessary. |