Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 7.8 g/cm³ Show Material materials with Dichte of 7.8 g/cm³ | typical value |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 16 % Show Material materials with Dehnung of 16 % | min., A5.65 |
Elastizitätsmodul | 23.0 °C | 190 - 210 GPa Show Material materials with Elastizitätsmodul of 190 - 210 GPa | typical value |
Flächenreduzierung | 23.0 °C | 32 % Show Material materials with Flächenreduzierung of 32 % | min. |
Kerbschlagenergie | -40.0 °C | 27 J Show Material materials with Kerbschlagenergie of 27 J | min. |
Poissonzahl | 23.0 °C | 0.3 [-] Show Material materials with Poissonzahl of 0.3 [-] | typical value |
Streckgrenze | 23.0 °C | 590 MPa Show Material materials with Streckgrenze of 590 MPa | min |
Zugfestigkeit | 23.0 °C | 700 - 850 MPa Show Material materials with Zugfestigkeit of 700 - 850 MPa |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.33E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.33E-5 1/K | Typical for Manganese Steel |
Schmelzpunkt | 1382 - 1529 °C Show Material materials with Schmelzpunkt of 1382 - 1529 °C | Typical for Manganese Steel | |
Spezifische Wärmekapazität | 23.0 °C | 510 - 553 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 510 - 553 J/(kg·K) | Typical for Manganese Steel |
Wärmeleitfähigkeit | 23.0 °C | 14 - 16 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 14 - 16 W/(m·K) | Typical for Manganese Steel |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Eisen | Balance | ||
Kohlenstoff | 0.16 - 0.22 % Show Material materials with Kohlenstoff of 0.16 - 0.22 % | ||
Mangan | 1.3 - 1.7 % Show Material materials with Mangan of 1.3 - 1.7 % | ||
Phosphor | 0.04 % Show Material materials with Phosphor of 0.04 % | max. | |
Schwefel | 0.035 % Show Material materials with Schwefel of 0.035 % | max. | |
Silizium | 0.1 - 0.5 % Show Material materials with Silizium of 0.1 - 0.5 % | ||
Vanadium | 0.1 - 0.2 % Show Material materials with Vanadium of 0.1 - 0.2 % | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Typical applications are: Chrome plating, cylinders, conveyor rolls, hollow shafts, nuts, rings. | |
| General machinability | Excellent | |
| Welding | Excellent | |