Property | Value | Comment |
---|---|---|
Carbon equivalent (CET) | 0.4 [-] Show Material materials with Carbon equivalent (CET) of 0.4 [-] | |
Carbon equivalent (CEV) | 0.64 [-] Show Material materials with Carbon equivalent (CEV) of 0.64 [-] | for t ≤ 50 mm plate thickness |
0.66 [-] Show Material materials with Carbon equivalent (CEV) of 0.66 [-] | for 50 < t ≤100 mm plate thickness | |
0.68 [-] Show Material materials with Carbon equivalent (CEV) of 0.68 [-] | t ≤ 65 mm tabulars | |
0.7 [-] Show Material materials with Carbon equivalent (CEV) of 0.7 [-] | for 100 < t ≤ 250 mm plate thickness | |
Dichte | 7.8 - 7.9 g/cm³ Show Material materials with Dichte of 7.8 - 7.9 g/cm³ | typical for low carbon steel |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | -20 °C | 62 J Show Material materials with Charpy impact energy, V-notch of 62 J | min. |
Charpy impact energy, V-notch, transverse | -20 °C | 46 J Show Material materials with Charpy impact energy, V-notch, transverse of 46 J | min. |
Dehnung | 14 % Show Material materials with Dehnung of 14 % | min., Transverse | |
16 % Show Material materials with Dehnung of 16 % | min. | ||
Elastizitätsmodul | 200 - 215 GPa Show Material materials with Elastizitätsmodul of 200 - 215 GPa | typical for low carbon steel | |
Poissonzahl | 0.29 [-] Show Material materials with Poissonzahl of 0.29 [-] | typical for low carbon steel | |
Schubmodule | 82 GPa Show Material materials with Schubmodule of 82 GPa | typical for low carbon steel | |
Zugfestigkeit | 770 - 940 MPa Show Material materials with Zugfestigkeit of 770 - 940 MPa |
Thermisch
Property | Value | Comment |
---|---|---|
Koeffizient der thermischen Ausdehnung | 1.32e-05 - 1.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.32e-05 - 1.38e-05 1/K | typical for low carbon steel |
Max. Betriebstemperatur | 500 °C Show Material materials with Max. Betriebstemperatur of 500 °C | typical for carbon steel |
Schmelzpunkt | 1480 - 1526 °C Show Material materials with Schmelzpunkt of 1480 - 1526 °C | typical for low carbon steel |
Spezifische Wärmekapazität | 465 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 465 J/(kg·K) | typical for low carbon steel |
Wärmeleitfähigkeit | 25 - 93 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 25 - 93 W/(m·K) | typical for low carbon steel |
Elektrisch
Property | Value | Comment |
---|---|---|
spezifischer Widerstand | 1.43e-07 - 1.74e-07 Ω·m Show Material materials with spezifischer Widerstand of 1.43e-07 - 1.74e-07 Ω·m | typical for carbon steel |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminium | 0.018 % Show Material materials with Aluminium of 0.018 % | min. |
Chrom | 1.5 % Show Material materials with Chrom of 1.5 % | |
Kohlenstoff | 0.18 % Show Material materials with Kohlenstoff of 0.18 % | |
Kupfer | 0.5 % Show Material materials with Kupfer of 0.5 % | |
Mangan | 1.7 % Show Material materials with Mangan of 1.7 % | |
Molybdän | 0.7 % Show Material materials with Molybdän of 0.7 % | |
Nickel | 2 % Show Material materials with Nickel of 2 % | higher Ni content may be qualified and accepted subject to qualification during manufacturer qualification testing |
Niobium | 0.06 % Show Material materials with Niobium of 0.06 % | |
Phosphor | 0.025 % Show Material materials with Phosphor of 0.025 % | can be 0.005% higher than the specified value |
Schwefel | 0.015 % Show Material materials with Schwefel of 0.015 % | can be 0.005% higher than the specified value |
Silizium | 0.8 % Show Material materials with Silizium of 0.8 % | |
Stickstoff | 0.015 % Show Material materials with Stickstoff of 0.015 % | the total aluminium to nitrogen ratio shall be a minimum of 2:1. When other nitrogen binding elements are used, the minimum Al value and Al/N ratio do not apply |
Titan | 0.05 % Show Material materials with Titan of 0.05 % | |
Vanadium | 0.12 % Show Material materials with Vanadium of 0.12 % |
Technological properties
Property | ||
---|---|---|
Supplier Disclaimer | The given information is a rough description and some properties can depend on various factors such as product thickness. Please contact the supplier or refer to the related norm or standard for further information. |