EN 12165 Grade CuZn40Mn2Fe1 H080

Want to keep this datasheet? Save it now in your required format

Description

CuZn40Mn2Fe1(former identification: CuZn40Mn2) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Tensile strength and Brinell hardness are higher than at CuZn31Si1 (CW708R). Manganese increases corrosion resistance and sliding qualities. CuZn40Mn2Fe1is weathering and seawater resistant. Processing properties: warm forming: good cold forming: moderately machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good Application in apparatus and general machine engineering, for fittings and refrigerators and for shock-absorber rods. In construction trade for weathering facades, for ornamental iron parts such as iron bars, gates or crosses.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

All categories

Eigenschaften

Mechanisch

Property	Temperature	Value	Comment
Dehnung	20.0 °C	15 % Show Material materials with Dehnung of 15 %
Elastizitätsmodul	23.0 °C	100 - 125 GPa Show Material materials with Elastizitätsmodul of 100 - 125 GPa	Typical for Wrought Copper Brass
Härte, Brinell	20.0 °C	80 [-] Show Material materials with Härte, Brinell of 80 [-]
Härte, Vickers	20.0 °C	85 [-] Show Material materials with Härte, Vickers of 85 [-]
Schubmodule	23.0 °C	40 GPa Show Material materials with Schubmodule of 40 GPa	Typical for Wrought Copper Brass
Streckgrenze Rp 0,2	20.0 °C	160 MPa Show Material materials with Streckgrenze Rp 0,2 of 160 MPa
Zugfestigkeit	20.0 °C	350 MPa Show Material materials with Zugfestigkeit of 350 MPa

Thermisch

Property	Temperature	Value	Comment
Koeffizient der thermischen Ausdehnung	23.0 °C	1.7E-5 - 2.1E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Schmelzpunkt		875 - 1075 °C Show Material materials with Schmelzpunkt of 875 - 1075 °C	Typical for Wrought Copper Brass
Spezifische Wärmekapazität	23.0 °C	371 - 418 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 371 - 418 J/(kg·K)	Typical for Wrought Copper Brass
Wärmeleitfähigkeit	23.0 °C	100 - 234 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 100 - 234 W/(m·K)	Typical for Wrought Copper Brass

Chemical properties

Property	Value
Aluminium	0.1 % Show Material materials with Aluminium of 0.1 %
Blei	0.8 % Show Material materials with Blei of 0.8 %
Eisen	1.5 % Show Material materials with Eisen of 1.5 %
Kupfer	57 - 59 % Show Material materials with Kupfer of 57 - 59 %
Mangan	1 - 2.5 % Show Material materials with Mangan of 1 - 2.5 %
Nickel	1 % Show Material materials with Nickel of 1 %
Silizium	0.1 % Show Material materials with Silizium of 0.1 %
Zinn	0.5 % Show Material materials with Zinn of 0.5 %