EN 12167 Grade CuZn40Mn2Fe1 H105

Want to keep this datasheet? Save it now in your required format

Description

CuZn40Mn2Fe1(former identification: CuZn40Mn2) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Tensile strength and Brinell hardness are higher than at CuZn31Si1 (CW708R). Manganese increases corrosion resistance and sliding qualities. CuZn40Mn2Fe1is weathering and seawater resistant. Processing properties: warm forming: good cold forming: moderately machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good Application in apparatus and general machine engineering, for fittings and refrigerators and for shock-absorber rods. In construction trade for weathering facades, for ornamental iron parts such as iron bars, gates or crosses.

Related Standards

Equivalent Materials

Diese Materialdaten wurden von WIAM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Temperature	Value
Dichte	20.0 °C	8.35 g/cm³ Show Material materials with Dichte of 8.35 g/cm³

Mechanisch

Property	Temperature	Value
Elastizitätsmodul	20.0 °C	100 GPa Show Material materials with Elastizitätsmodul of 100 GPa
Härte, Brinell	20.0 °C	105 [-] Show Material materials with Härte, Brinell of 105 [-]
Härte, Vickers	20.0 °C	110 [-] Show Material materials with Härte, Vickers of 110 [-]
Schubmodule	20.0 °C	38 GPa Show Material materials with Schubmodule of 38 GPa

Thermisch

Property	Temperature	Value	Comment
Koeffizient der thermischen Ausdehnung	200.0 °C	1.85E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.85E-5 1/K
Schmelzpunkt		875 - 1075 °C Show Material materials with Schmelzpunkt of 875 - 1075 °C	Typical for Wrought Copper Brass
Spezifische Wärmekapazität	20.0 °C	377 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 377 J/(kg·K)
Wärmeleitfähigkeit	20.0 °C	67 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 67 W/(m·K)

Elektrisch

Property	Temperature	Value
Elektrische Leitfähigkeit	20.0 °C	8.60E+6 S/m Show Material materials with Elektrische Leitfähigkeit of 8.60E+6 S/m
spezifischer Widerstand	20.0 °C	1.16E-7 Ω·m Show Material materials with spezifischer Widerstand of 1.16E-7 Ω·m

Chemical properties

Property	Value
Aluminium	0.1 % Show Material materials with Aluminium of 0.1 %
Blei	0.8 % Show Material materials with Blei of 0.8 %
Eisen	1.5 % Show Material materials with Eisen of 1.5 %
Kupfer	57 - 59 % Show Material materials with Kupfer of 57 - 59 %
Mangan	1 - 2.5 % Show Material materials with Mangan of 1 - 2.5 %
Nickel	1 % Show Material materials with Nickel of 1 %
Silizium	0.1 % Show Material materials with Silizium of 0.1 %
Zinn	0.5 % Show Material materials with Zinn of 0.5 %