General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.1 g/cm³ Show Material materials with Densidad of 8.1 g/cm³ |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 23.0 °C | 150 [-] Show Material materials with Dureza Brinell of 150 [-] |
Dureza Vickers | 23.0 °C | 150 [-] Show Material materials with Dureza Vickers of 150 [-] |
Elongación | 23.0 °C | 15 % Show Material materials with Elongación of 15 % |
Límite elástico Rp 0,2 | 23.0 °C | 280 MPa Show Material materials with Límite elástico Rp 0,2 of 280 MPa |
Módulo elástico | 23.0 °C | 93 GPa Show Material materials with Módulo elástico of 93 GPa |
Resistencia a la tracción | 23.0 °C | 540 MPa Show Material materials with Resistencia a la tracción of 540 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 20.0 °C | 2.04E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.04E-5 1/K |
100.0 °C | 2.04E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.04E-5 1/K | |
Conductividad térmica | 23.0 °C | 63 W/(m·K) Show Material materials with Conductividad térmica of 63 W/(m·K) |
Temperatura de fusión | 865 - 885 °C Show Material materials with Temperatura de fusión of 865 - 885 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 7.80E+6 S/m Show Material materials with Conductividad eléctrica of 7.80E+6 S/m |
Resistividad eléctrica | 23.0 °C | 1.28E-7 Ω·m Show Material materials with Resistividad eléctrica of 1.28E-7 Ω·m |
Chemical properties
Property | Value |
---|---|
Aluminio | 1.3 - 2.3 % Show Material materials with Aluminio of 1.3 - 2.3 % |
Cobre | 57 - 59 % Show Material materials with Cobre of 57 - 59 % |
Estaño | 0.4 % Show Material materials with Estaño of 0.4 % |
Hierro | 1 % Show Material materials with Hierro of 1 % |
Manganeso | 1.5 - 3 % Show Material materials with Manganeso of 1.5 - 3 % |
Níquel | 1 % Show Material materials with Níquel of 1 % |
Otro | Rest Zn, total 0.3 |
Plomo | 0.2 - 0.8 % Show Material materials with Plomo of 0.2 - 0.8 % |
Silicona | 0.3 - 1.3 % Show Material materials with Silicona of 0.3 - 1.3 % |
Technological properties
Property | ||
---|---|---|
Brazing | hard brazing : wenig geeignet, soft brazing: wenig geeignet | |
Workability | Cold forming degree between anneals: max. 15 %, general (condition): limited |