General
Property | Value | Testing Standard | Condition |
---|---|---|---|
Absorción de agua | 1.4 % Show Supplier Material materials with Absorción de agua of 1.4 % | Sim. to ISO 62 | |
Bio-based content | 97 % Show Supplier Material materials with Bio-based content of 97 % | ||
Densidad | 1.25 g/cm³ Show Supplier Material materials with Densidad of 1.25 g/cm³ | ISO 1183 | dry |
Moisture absorption | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | Sim. to ISO 62 | |
Índice límite de óxigeno | 22 % Show Supplier Material materials with Índice límite de óxigeno of 22 % | ISO 4589-1/-2 | dry |
Mecánica
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Dureza Shore D | 74 [-] Show Supplier Material materials with Dureza Shore D of 74 [-] | dry | ISO 7619-1 | 15 seconds | |
Elongación | 6 % Show Supplier Material materials with Elongación of 6 % | cond. | ISO 527-1/-2 | ||
Módulo elástico | 7.3 GPa Show Supplier Material materials with Módulo elástico of 7.3 GPa | cond. | ISO 527-1/-2 | ||
Resistencia a la tracción | 117 MPa Show Supplier Material materials with Resistencia a la tracción of 117 MPa | cond. | ISO 527-1/-2 | ||
Resistencia al choque, ensayo Charpy entallado | -30 °C | 17 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 17 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 24 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 24 kJ/m² | cond. | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | -30 °C | 96 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 96 kJ/m² | cond. | ISO 179/1eU | |
23 °C | 89 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 89 kJ/m² | cond. | ISO 179/1eU |
Aplicaciones térmicas
Property | Value | Condition | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 5e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5e-05 1/K | dry | ISO 11359-1/-2 | ||||
Temperatura de fusión | 189 °C Show Supplier Material materials with Temperatura de fusión of 189 °C | dry | ISO 11357-1/-3 | 10°C/min | |||
Temperatura de reblandecimiento Vicat | 170 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 170 °C | ISO 306 | 50°C/h 50N | ||||
Inflamabilidad | At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB |
Eléctrico
Property | Value | Condition | Frequency | Testing Standard |
---|---|---|---|---|
Constante dieléctrica | 4 [-] Show Supplier Material materials with Constante dieléctrica of 4 [-] | dry | 100Hz | IEC 60250 |
4 [-] Show Supplier Material materials with Constante dieléctrica of 4 [-] | dry | 1MHz | IEC 60250 | |
Factor de disipación | 0.021 [-] Show Supplier Material materials with Factor de disipación of 0.021 [-] | dry | 1MHz | IEC 60250 |
0.0578 [-] Show Supplier Material materials with Factor de disipación of 0.0578 [-] | dry | 100Hz | IEC 60250 | |
Rigidez dieléctrica | 45 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 45 kV/mm | cond. | IEC 60243-1 | |
Surface resistivity | 1e+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+14 Ω/sq | cond. | IEC 60093 | |
Volume resistivity | 7e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 7e+11 Ω·cm | cond. | IEC 60093 | |
Índice de seguimiento comparativo | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | cond. | IEC 60112 |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Velocidad de flujo del volumen derretido | 9 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 9 cm³/10min | dry | ISO 1133 | 235°C/5kg |
Technological properties
Property | ||
---|---|---|
Application areas | Connectors,Footwear - Outsoles,Sports Equipment | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding: |