Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.79 g/cm³ Show Supplier Material materials with Densidad of 7.79 g/cm³ |
Estructura de grano | Bainidur 1300 allows a process-reliable adjustment of the bainitic microstructure even for large components (> 60 mm rd.) with consistently high quality. |
Mecánica
| Property | Value |
|---|---|
Charpy impact energy, V-notch | 20 - 50 J Show Supplier Material materials with Charpy impact energy, V-notch of 20 - 50 J |
Dureza Rockwell C | 36 - 40 [-] Show Supplier Material materials with Dureza Rockwell C of 36 - 40 [-] |
Límite elástico | 600 - 900 MPa Show Supplier Material materials with Límite elástico of 600 - 900 MPa |
Módulo elástico | 205 GPa Show Supplier Material materials with Módulo elástico of 205 GPa |
Resistencia a la tracción | 1000 - 1300 MPa Show Supplier Material materials with Resistencia a la tracción of 1000 - 1300 MPa |
Aplicaciones térmicas
| Property | Value |
|---|---|
Calor específico | 460 J/(kg·K) Show Supplier Material materials with Calor específico of 460 J/(kg·K) |
Conductividad térmica | 44.5 W/(m·K) Show Supplier Material materials with Conductividad térmica of 44.5 W/(m·K) |
Chemical properties
| Property | Value |
|---|---|
Boro | traces |
Carbono | 0.12 - 0.25 % Show Supplier Material materials with Carbono of 0.12 - 0.25 % |
Cromo | 0.8 - 1.5 % Show Supplier Material materials with Cromo of 0.8 - 1.5 % |
Hierro | Balance |
Manganeso | 1.2 - 1.5 % Show Supplier Material materials with Manganeso of 1.2 - 1.5 % |
Molibdeno | 0.5 - 1.1 % Show Supplier Material materials with Molibdeno of 0.5 - 1.1 % |
Silicona | 0.5 - 1.3 % Show Supplier Material materials with Silicona of 0.5 - 1.3 % |
Vanadio | 0.05 - 0.15 % Show Supplier Material materials with Vanadio of 0.05 - 0.15 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Bainidur® 1300 was developed for forging parts with highest requirements. | |
| General machinability | Very good | |
| Processing history | The powder is produced by gas atomization. | |
| Welding | Due to the low carbon content Bainidur® 1300 has a superior weldability. The formation latent heat during the bainitic transformation reduces thermal stresses and therefor the risk of cracking. | |