General
Property | Value |
---|---|
Densidad | 7.4 g/cm³ Show Supplier Material materials with Densidad of 7.4 g/cm³ |
Estructura de grano | Titanium carbide + austenite |
Mecánica
Property | Value |
---|---|
Dureza Rockwell C | 54 [-] Show Supplier Material materials with Dureza Rockwell C of 54 [-] |
Módulo elástico | 277 GPa Show Supplier Material materials with Módulo elástico of 277 GPa |
Resistencia a la compresión | 1500 MPa Show Supplier Material materials with Resistencia a la compresión of 1500 MPa |
Resistencia a la flexión | 1300 MPa Show Supplier Material materials with Resistencia a la flexión of 1300 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 100 °C | 9e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9e-06 1/K | for 20°C to the mentioned temperature |
200 °C | 1e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.05e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.05e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.08e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.08e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.11e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.11e-05 1/K | for 20°C to the mentioned temperature | |
600 °C | 1.15e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.15e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 12.4 W/(m·K) Show Supplier Material materials with Conductividad térmica of 12.4 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 1.53e-06 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.53e-06 Ω·m |
Magnético
Property | Value | Comment |
---|---|---|
Permeabilidad magnética relativa | 1 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 1 [-] | max. |
Chemical properties
Technological properties
Property | ||
---|---|---|
Application areas | This austenitic grade is used for applications requiring complete non-magnetisability, a high wear resistance and maximum corrosion resistance. | |
Corrosion properties | Besides having a high wear resistance, this alloy is extremely resistant to corrosion and scaling, as well as highly tempering-resistant. This corrosion resistance is at its best with finely ground or polished surfaces. | |
General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
Heat Treatment | Solution Anealing: 1200°C, 2 hr in vacuum (Cooling 4 bar N2) Hardness: 52 HRC - Age-Hardening 800°C, 6 hr in Vacuum, Hardness: 54 HRC |