Propiedades
General
| Property | Value |
|---|---|
Densidad | 6.7 g/cm³ Show Supplier Material materials with Densidad of 6.7 g/cm³ |
Estructura de grano | Titanium carbide + nickel martensite |
Mecánica
| Property | Value |
|---|---|
Dureza Rockwell C | 63 [-] Show Supplier Material materials with Dureza Rockwell C of 63 [-] |
Módulo de cizallamiento | 117 GPa Show Supplier Material materials with Módulo de cizallamiento of 117 GPa |
Módulo elástico | 280 GPa Show Supplier Material materials with Módulo elástico of 280 GPa |
Resistencia a la compresión | 2400 MPa Show Supplier Material materials with Resistencia a la compresión of 2400 MPa |
Resistencia a la flexión | 1450 MPa Show Supplier Material materials with Resistencia a la flexión of 1450 MPa |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 100 °C | 8e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8e-06 1/K | for 20°C to the mentioned temperature |
200 °C | 8.7e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.7e-06 1/K | for 20°C to the mentioned temperature | |
300 °C | 8.9e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.9e-06 1/K | for 20°C to the mentioned temperature | |
400 °C | 9.1e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.1e-06 1/K | for 20°C to the mentioned temperature | |
500 °C | 9.4e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.4e-06 1/K | for 20°C to the mentioned temperature | |
600 °C | 9.8e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.8e-06 1/K | for 20°C to the mentioned temperature | |
700 °C | 9.4e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.4e-06 1/K | for 20°C to the mentioned temperature | |
800 °C | 8.5e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.5e-06 1/K | for 20°C to the mentioned temperature | |
900 °C | 9.2e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.2e-06 1/K | for 20°C to the mentioned temperature | |
1000 °C | 9.7e-06 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.7e-06 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 18.1 - 18.9 W/(m·K) Show Supplier Material materials with Conductividad térmica of 18.1 - 18.9 W/(m·K) | 20-80°C |
Eléctrico
| Property | Value |
|---|---|
Resistividad eléctrica | 8.06e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 8.06e-07 Ω·m |
Magnético
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | In heat-treated, hardened condition (up to 69 HRC), Ferro-Titanit® can be used to solve many wear problems economically. | |
| General machinability | In as-delivered condition, this material can be machined by conventional methods. | |
| Heat Treatment | Annealing: 850°C, 2-4 hr in vacuum (Cooling 1-4.5 bar N2) Hardness: 53 HRC - Age-Hardening 480°C, 6-8 hr, Hardness: 63 HRC | |