Property | Value |
---|---|
Densidad | 8 g/cm³ Show Supplier Material materials with Densidad of 8 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro | 250 mm Show Supplier Material materials with Diámetro of 250 mm | max. |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 100 J Show Supplier Material materials with Charpy impact energy, V-notch of 100 J | ||
Dureza Brinell | 215 [-] Show Supplier Material materials with Dureza Brinell of 215 [-] | ||
Dureza Rockwell C | 22 [-] Show Supplier Material materials with Dureza Rockwell C of 22 [-] | ||
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | A5 | Transverse | |
40 % Show Supplier Material materials with Elongación of 40 % | A5 | ||
Límite elástico | 20 °C | 200 MPa Show Supplier Material materials with Límite elástico of 200 MPa | RP02 |
23 °C | 235 MPa Show Supplier Material materials with Límite elástico of 235 MPa | RP1 | |
100 °C | 165 MPa Show Supplier Material materials with Límite elástico of 165 MPa | RP02 | |
100 °C | 200 MPa Show Supplier Material materials with Límite elástico of 200 MPa | RP1 | |
150 °C | 150 MPa Show Supplier Material materials with Límite elástico of 150 MPa | RP02 | |
150 °C | 180 MPa Show Supplier Material materials with Límite elástico of 180 MPa | RP1 | |
200 °C | 137 MPa Show Supplier Material materials with Límite elástico of 137 MPa | RP02 | |
200 °C | 165 MPa Show Supplier Material materials with Límite elástico of 165 MPa | RP1 | |
250 °C | 127 MPa Show Supplier Material materials with Límite elástico of 127 MPa | RP02 | |
250 °C | 153 MPa Show Supplier Material materials with Límite elástico of 153 MPa | RP1 | |
300 °C | 119 MPa Show Supplier Material materials with Límite elástico of 119 MPa | RP02 | |
300 °C | 145 MPa Show Supplier Material materials with Límite elástico of 145 MPa | RP1 | |
350 °C | 113 MPa Show Supplier Material materials with Límite elástico of 113 MPa | RP02 | |
350 °C | 139 MPa Show Supplier Material materials with Límite elástico of 139 MPa | RP1 | |
400 °C | 108 MPa Show Supplier Material materials with Límite elástico of 108 MPa | RP02 | |
400 °C | 135 MPa Show Supplier Material materials with Límite elástico of 135 MPa | RP1 | |
450 °C | 103 MPa Show Supplier Material materials with Límite elástico of 103 MPa | RP02 | |
450 °C | 130 MPa Show Supplier Material materials with Límite elástico of 130 MPa | RP1 | |
500 °C | 100 MPa Show Supplier Material materials with Límite elástico of 100 MPa | RP02 | |
500 °C | 128 MPa Show Supplier Material materials with Límite elástico of 128 MPa | RP1 | |
550 °C | 98 MPa Show Supplier Material materials with Límite elástico of 98 MPa | RP02 | |
550 °C | 127 MPa Show Supplier Material materials with Límite elástico of 127 MPa | RP1 | |
Módulo elástico | 20 °C | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | |
100 °C | 194 GPa Show Supplier Material materials with Módulo elástico of 194 GPa | ||
200 °C | 186 GPa Show Supplier Material materials with Módulo elástico of 186 GPa | ||
300 °C | 179 GPa Show Supplier Material materials with Módulo elástico of 179 GPa | ||
400 °C | 172 GPa Show Supplier Material materials with Módulo elástico of 172 GPa | ||
500 °C | 165 GPa Show Supplier Material materials with Módulo elástico of 165 GPa | ||
Resistencia a la tracción | 500 - 700 MPa Show Supplier Material materials with Resistencia a la tracción of 500 - 700 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 500 J/(kg·K) Show Supplier Material materials with Calor específico of 500 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.6e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.6e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.65e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.65e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.7e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.7e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.75e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.8e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.8e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 15 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 7.5e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 7.5e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Azufre | 0.03 % Show Supplier Material materials with Azufre of 0.03 % |
Carbono | 0.03 % Show Supplier Material materials with Carbono of 0.03 % |
Cromo | 16.5 - 18.5 % Show Supplier Material materials with Cromo of 16.5 - 18.5 % |
Fósforo | 0.045 % Show Supplier Material materials with Fósforo of 0.045 % |
Hierro | Balance |
Manganeso | 2 % Show Supplier Material materials with Manganeso of 2 % |
Molibdeno | 2 - 2.5 % Show Supplier Material materials with Molibdeno of 2 - 2.5 % |
Nitrógeno | 0.1 % Show Supplier Material materials with Nitrógeno of 0.1 % |
Níquel | 10 - 13 % Show Supplier Material materials with Níquel of 10 - 13 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Technological properties
Property | ||
---|---|---|
Application areas | Chemical Industry, Pharmaceutical Industry, Food Industry, Fittings, Construction, Ship Building & Marine Structures, Petrochemistry, Automotive, Decorative Applications, Kitchen Equipment, Electronics, Aerospace, Maritime | |
Cold Forming | It is suitable for cold forming according to DIN EN 10263-5. | |
Corrosion properties | Due to the molybdenum content has a higher corrosion resistance thatn Acidur 4301 and 4307 (specially in chloride mediums). Due to its low carbon content it is resistant against intergranular corrosion according to DIN EN 3651 part 2. PREN= 23.1-28.8 | |
Heat Treatment | Solution annealing: 1020-1120°C (water, air) fast cooling | |
Hot forming | It is formable at 900-1200°C | |
Processing history | Solution Annealed | |
Welding | It is weldable with or without filler material (e.g. 1.4430). The interpass temperature should not exceed 200°C. Subsequent heat treatment is not require. The resistance to intergranular corrosion is not affected by welding according to DIN EN 3651 part 2. |