General
Property | Value |
---|---|
Densidad | 8 g/cm³ Show Supplier Material materials with Densidad of 8 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro | 250 mm Show Supplier Material materials with Diámetro of 250 mm | max. |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 100 J Show Supplier Material materials with Charpy impact energy, V-notch of 100 J | ||
Dureza Brinell | 215 [-] Show Supplier Material materials with Dureza Brinell of 215 [-] | ||
Dureza Rockwell C | 22 [-] Show Supplier Material materials with Dureza Rockwell C of 22 [-] | ||
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | A5 | Transverse | |
40 % Show Supplier Material materials with Elongación of 40 % | A5 | ||
Límite elástico | 20 °C | 200 MPa Show Supplier Material materials with Límite elástico of 200 MPa | RP02 |
23 °C | 235 MPa Show Supplier Material materials with Límite elástico of 235 MPa | RP1 | |
100 °C | 185 MPa Show Supplier Material materials with Límite elástico of 185 MPa | RP02 | |
100 °C | 215 MPa Show Supplier Material materials with Límite elástico of 215 MPa | RP1 | |
150 °C | 175 MPa Show Supplier Material materials with Límite elástico of 175 MPa | RP02 | |
150 °C | 205 MPa Show Supplier Material materials with Límite elástico of 205 MPa | RP1 | |
200 °C | 165 MPa Show Supplier Material materials with Límite elástico of 165 MPa | RP02 | |
200 °C | 192 MPa Show Supplier Material materials with Límite elástico of 192 MPa | RP1 | |
250 °C | 155 MPa Show Supplier Material materials with Límite elástico of 155 MPa | RP02 | |
250 °C | 183 MPa Show Supplier Material materials with Límite elástico of 183 MPa | RP1 | |
300 °C | 145 MPa Show Supplier Material materials with Límite elástico of 145 MPa | RP02 | |
300 °C | 175 MPa Show Supplier Material materials with Límite elástico of 175 MPa | RP1 | |
350 °C | 140 MPa Show Supplier Material materials with Límite elástico of 140 MPa | RP02 | |
350 °C | 169 MPa Show Supplier Material materials with Límite elástico of 169 MPa | RP1 | |
400 °C | 135 MPa Show Supplier Material materials with Límite elástico of 135 MPa | RP02 | |
400 °C | 160 MPa Show Supplier Material materials with Límite elástico of 160 MPa | RP1 | |
450 °C | 131 MPa Show Supplier Material materials with Límite elástico of 131 MPa | RP02 | |
450 °C | 160 MPa Show Supplier Material materials with Límite elástico of 160 MPa | RP1 | |
500 °C | 129 MPa Show Supplier Material materials with Límite elástico of 129 MPa | RP02 | |
500 °C | 158 MPa Show Supplier Material materials with Límite elástico of 158 MPa | RP1 | |
550 °C | 127 MPa Show Supplier Material materials with Límite elástico of 127 MPa | RP02 | |
550 °C | 157 MPa Show Supplier Material materials with Límite elástico of 157 MPa | RP1 | |
Módulo elástico | 20 °C | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | |
100 °C | 194 GPa Show Supplier Material materials with Módulo elástico of 194 GPa | ||
200 °C | 186 GPa Show Supplier Material materials with Módulo elástico of 186 GPa | ||
300 °C | 179 GPa Show Supplier Material materials with Módulo elástico of 179 GPa | ||
400 °C | 172 GPa Show Supplier Material materials with Módulo elástico of 172 GPa | ||
500 °C | 165 GPa Show Supplier Material materials with Módulo elástico of 165 GPa | ||
Resistencia a la tracción | 500 - 700 MPa Show Supplier Material materials with Resistencia a la tracción of 500 - 700 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 500 J/(kg·K) Show Supplier Material materials with Calor específico of 500 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.65e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.65e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.75e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.8e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.8e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.85e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.85e-05 1/K | for 20°C to the mentioned temperature | |
500 °C | 1.9e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.9e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 15 W/(m·K) Show Supplier Material materials with Conductividad térmica of 15 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 7.5e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 7.5e-07 Ω·m |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Azufre | 0.03 % Show Supplier Material materials with Azufre of 0.03 % | ||
Carbono | 0.08 % Show Supplier Material materials with Carbono of 0.08 % | ||
Cromo | 16.5 - 18.5 % Show Supplier Material materials with Cromo of 16.5 - 18.5 % | ||
Fósforo | 0.045 % Show Supplier Material materials with Fósforo of 0.045 % | ||
Hierro | Balance | ||
Manganeso | 2 % Show Supplier Material materials with Manganeso of 2 % | ||
Molibdeno | 2 - 2.5 % Show Supplier Material materials with Molibdeno of 2 - 2.5 % | ||
Níquel | 10.5 - 13.5 % Show Supplier Material materials with Níquel of 10.5 - 13.5 % | ||
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % | ||
Titanio | 0.7 % Show Supplier Material materials with Titanio of 0.7 % | min: 5xC |
Technological properties
Property | ||
---|---|---|
Application areas | Apparatus and pipeline construction, Construction industry, Chemical industry, Food industry, Mechanical Engineering, Medical and pharmaceutical industry, Shipbuilding | |
Corrosion properties | Acidur 4571 shows good corrosion resistance in most natural waters with low to medium concentrations of chlorides, salt and hydrochloric acid as well as organic acids. Since Acidur 4571 is resistant to intergranular corrosion even after welding, it meets the following standardized test methods: AFNOR NF 05-159, ASTM A262 Practice E and DIN EN ISO 3651 Part 2. (PREN = 23.1 – 26.7) | |
General machinability | The addition of titanium leads to the formation of titanium carbonitrides, which increases the tool wear | |
Heat Treatment | Solution annealing: 1020-1120°C (water, air) fast cooling | |
Hot forming | It is formable at 900-1200°C | |
Processing history | Solution Annealed | |
Welding | Acidur 4571 can be welded with and without filler material using all conventional methods. If a filler metal is necessary, use 1.4430. No heat treatment is required after welding. The interpass temperature should not exceed 200°C. Approach colours must be mechanically or chemically be removed. |