Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.7 g/cm³ Show Supplier Material materials with Densidad of 7.7 g/cm³ |
Medidas
| Property | Value | Comment |
|---|---|---|
Diámetro | 250 mm Show Supplier Material materials with Diámetro of 250 mm | max. |
Mecánica
| Property | Value | Comment |
|---|---|---|
Charpy impact energy, V-notch | 25 - 30 J Show Supplier Material materials with Charpy impact energy, V-notch of 25 - 30 J | |
Dureza Brinell | 248 [-] Show Supplier Material materials with Dureza Brinell of 248 [-] | annealed |
Elongación | 10 - 12 % Show Supplier Material materials with Elongación of 10 - 12 % | A5 |
Hardness, Vickers, 1 | 800 [-] Show Supplier Material materials with Hardness, Vickers, 1 of 800 [-] | nitrided |
Límite elástico | 675 - 835 MPa Show Supplier Material materials with Límite elástico of 675 - 835 MPa | |
Módulo elástico | 210 GPa Show Supplier Material materials with Módulo elástico of 210 GPa | |
Resistencia a la tracción | 880 - 1230 MPa Show Supplier Material materials with Resistencia a la tracción of 880 - 1230 MPa |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 430 J/(kg·K) Show Supplier Material materials with Calor específico of 430 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.15e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.15e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.25e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.25e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.33e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.33e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.39e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.39e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 42 W/(m·K) Show Supplier Material materials with Conductividad térmica of 42 W/(m·K) |
Eléctrico
| Property | Value |
|---|---|
Resistividad eléctrica | 1.9e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1.9e-07 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Azufre | 0.035 % Show Supplier Material materials with Azufre of 0.035 % |
Carbono | 0.28 - 0.35 % Show Supplier Material materials with Carbono of 0.28 - 0.35 % |
Cromo | 2.8 - 3.3 % Show Supplier Material materials with Cromo of 2.8 - 3.3 % |
Fósforo | 0.025 % Show Supplier Material materials with Fósforo of 0.025 % |
Hierro | Balance |
Manganeso | 0.4 - 0.7 % Show Supplier Material materials with Manganeso of 0.4 - 0.7 % |
Molibdeno | 0.3 - 0.5 % Show Supplier Material materials with Molibdeno of 0.3 - 0.5 % |
Silicona | 0.4 % Show Supplier Material materials with Silicona of 0.4 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | It is used in Automotive and Mechanical engineering for components such as gear wheels, drills, connecting rods or shafts. | |
| Heat Treatment | Soft annealing: 650-700°C, Quenching: 870-930°C (Oil or Water), Tempering: 580-700°C, Nitriding: 480-570°C | |
| Hot forming | It is formable at 900-1100°C. | |
| Processing history | Quenched and Tempered | |
| Welding | It is difficult to weld and should will not used be in welded constructions. | |