Nickel 99.98% Rod & Wire S-Annealed

Nombres alternativos y comerciales
N02270, 2.4050, N02200, N02201, 2.4060, 2.4061, 2.4066, 2.4068, N02205, Pure Nickel

Want to keep this datasheet? Save it now in your required format

Description

Nickel with highest degree of purity with the following features:

Very low levels of carbon (20 ppm) and sulfur (2 ppm) which tend to segregate at grain boundries resulting in hot shortening

Cleanliness, absence of non-metallic inclusions as Al, Ti or Si oxides

Low electrical resistivity at 20°C

High thermal conductivity at 20°C

Excellent formability

Low softening temperature (350°C)

Low recrystallization temperature (350°C)

Improved oxidation resistance: development of tightly adherent one-layer oxide scale instead of a two-layer costumary one, which tends to flake off due to mismatch in thermal expansion.

Equivalent Materials

Los datos sobre este material han sido proporcionados por Hpulcas GmbH.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Propiedades

Medidas

Property	Value
Dimensions	Rod: Diameter: up to 4.7 mm, Length: up to 2500 mm - Wire: Diameter: 0.2-1.6 mm ; various dimensions can be also customized

Mecánica

Property	Temperature	Value	Comment
Dureza Vickers	23.0 °C	65 [-] Show Supplier Material materials with Dureza Vickers of 65 [-]	max.
Módulo elástico	23.0 °C	196 GPa Show Supplier Material materials with Módulo elástico of 196 GPa

Aplicaciones térmicas

Property	Temperature	Value
Conductividad térmica	23.0 °C	90.9 - 91 W/(m·K) Show Supplier Material materials with Conductividad térmica of 90.9 - 91 W/(m·K)
Recrystallization temperature		350 °C Show Supplier Material materials with Recrystallization temperature of 350 °C

Eléctrico

Property	Temperature	Value
Resistividad eléctrica	23.0 °C	7.1E-8 Ω·m Show Supplier Material materials with Resistividad eléctrica of 7.1E-8 Ω·m

Chemical properties

Property	Value
Azufre	2E-4 % Show Supplier Material materials with Azufre of 2E-4 %
Carbono	2E-3 % Show Supplier Material materials with Carbono of 2E-3 %
Níquel	99.98 % Show Supplier Material materials with Níquel of 99.98 %

Technological properties

Property
Application areas	Wire: Sputter Targets, evaporation pellets, regulator coil in glow plugs of diesel engines; litz wire for current conduction under elevated temperatures and in aggressive environments, Pre material for thin wire manfacturing, Ni wire mesh, Thermal Spraying, Coating layer for corrosion protection from alkalis; salt spray; molten salt and reduciing chemicals; coating layer for high temperature resistance; corrosion protection at high temperatures; coating layer for membrane walls of power plants
Heat Treatment	Soft Annealed
Processing history	For producing wire, the 6 mm hot rolled thick plates are cut into 6 mm wide sticks. The sticks are frontally welded. Afterwards the raw wire can be treated in the same way as hot rolled wire produced by melt metallurgy. accordingly, the wire is drawn to the desired dimensions through cold drawing and intermediate annealing.
Surface Finish	Blank/Bare/bright surface