General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.04 g/cm³ Show Material materials with Densidad of 1.04 g/cm³ | ASTM D792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 24 % Show Material materials with Elongación of 24 % | ASTM D638 |
Elongation at yield | 23.0 °C | 2 % Show Material materials with Elongation at yield of 2 % | ASTM D638 |
Flexural yield strength | 23.0 °C | 70 MPa Show Material materials with Flexural yield strength of 70 MPa | ASTM D790 |
Impact strength, Izod notched, ASTM | 23.0 °C | 320 J/m Show Material materials with Impact strength, Izod notched, ASTM of 320 J/m | ASTM D256 |
Límite elástico | 23.0 °C | 44 MPa Show Material materials with Límite elástico of 44 MPa | ASTM D638 |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ASTM D790 |
Módulo elástico | 23.0 °C | 2.27 GPa Show Material materials with Módulo elástico of 2.27 GPa | ASTM D790 |
Resistencia a la tracción | 23.0 °C | 33 MPa Show Material materials with Resistencia a la tracción of 33 MPa | ASTM D638 |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 26 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 26 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A |
23.0 °C | 22 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 22 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.82E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8.82E-5 1/K | ASTM E831, for -40 to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.82E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.82E-5 1/K | ASTM E831, for -40 to 40°C | ||
Heat deflection temperature, 0.45 MPa | 94 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 94 °C | ASTM D648 | |||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ASTM D648 | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746 | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746 | |||
Temperatura de fusión | 220 - 260 °C Show Material materials with Temperatura de fusión of 220 - 260 °C | ||||
Temperatura de reblandecimiento Vicat | 98 °C Show Material materials with Temperatura de reblandecimiento Vicat of 98 °C | ISO 906, Rate B/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating (3) 1.5 mm UL 94 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 5.6 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 5.6 g/10min | ASTM D1238 230°C/3.8 kgf |
Velocidad de flujo del volumen derretido | 18 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 18 cm³/10min | ISO 1133, 220°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Additive manufacturing, Appliances, Automotive exterior parts, Construction applications, Electronic displays, Fluid handling, Lawn and garden equipment, Lenses, Lighting applications, medical/healthcare, Non-specific food, Outdoor applications, packaging | |
Color | Black, White, Natural (unpigmented) | |
Processing methods | Injection Molding: Drying Temperature: 80-95°C, Drying Time: 2-4 hr, Rear Temperature: 190-210°C, Middle Temperature: 205-225°C, Front Temperature: 215-240°C, Nozzle Temperature: 220-260°C, Melt Temperature: 220-260°C, Mold Temperature: 50-70°C, Back Pressure: 0.3-0.7 MPa, Screw Speed 30-60 rpm |