General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.68 % Show Material materials with Absorción de agua of 0.68 % | ISO 62 |
Absorción de agua, saturación | 23.0 °C | 7.8 % Show Material materials with Absorción de agua, saturación of 7.8 % | |
Coefficient of friction | 0.35 - 0.45 [-] Show Material materials with Coefficient of friction of 0.35 - 0.45 [-] | ISO 7148-2 | |
Densidad | 23.0 °C | 1.15 g/cm³ Show Material materials with Densidad of 1.15 g/cm³ | ISO 1183-1 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Rockwell M | 23.0 °C | 88 [-] Show Material materials with Dureza Rockwell M of 88 [-] | ISO 2039-2 | ||
Elongación | 23.0 °C | 20 % Show Material materials with Elongación of 20 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ISO 527-1, ISO 527-2 | ||
Módulo de flexión | 23.0 °C | 3.2 GPa Show Material materials with Módulo de flexión of 3.2 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 3.6 GPa Show Material materials with Módulo elástico of 3.6 GPa | ISO 527-1, ISO 527-2 | ||
Resistencia a la flexión | 23.0 °C | 128 MPa Show Material materials with Resistencia a la flexión of 128 MPa | ISO 178 | ||
Resistencia a la tracción | 23.0 °C | 95 MPa Show Material materials with Resistencia a la tracción of 95 MPa | ISO 527-1/-2 | ||
Set de compresión | 23.0 °C | 32 - 100 [-] Show Material materials with Set de compresión of 32 - 100 [-] | For 1-5 nominal strain | ||
Resistencia al choque, ensayo Charpy no entallado | No break; ISO 179-1/1eU | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 60.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 8E-5 1/K | Average value between 23°C and the mentioned Temperature | ||
100.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | Average value between 23°C and the mentioned Temperature | |||
Heat deflection temperature, 1.80 MPa | 85 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 260 °C Show Material materials with Temperatura de fusión of 260 °C | ISO 11357-1/-3 | |||
Temperatura máx. de funcionamiento | 80 °C Show Material materials with Temperatura máx. de funcionamiento of 80 °C | For min. 20,000 h | |||
Temperatura mín. de funcionamiento | -20 °C Show Material materials with Temperatura mín. de funcionamiento of -20 °C | ||||
Inflamabilidad | UL 94 (3 mm thickness) HB | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.3 [-] Show Material materials with Constante dieléctrica of 3.3 [-] | IEC 60250, at 1MHz |
Resistividad eléctrica | 23.0 °C | 1.00E+12 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+12 Ω·m | IEC 60093 |
Rigidez dieléctrica | 23.0 °C | 26 kV/mm Show Material materials with Rigidez dieléctrica of 26 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | ANIS/ESD STM 11.11 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Gears, Sprockets, Star wheels, Bushings, Bearings, Wear Pads, Rails and Strips, Pulleys, Sheaves andGuides, Conveyor Wheels, Rollers and Sleeves, Supports Blocks, Valve Seats, Valve seals | |
| Color | Grey | |
| Fillers | Molybdenum disulfide (MoS2) | |