General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.05 % Show Material materials with Absorción de agua of 0.05 % | ASTM D 570 | 24 Hours |
Densidad | 23.0 °C | 1.52 g/cm³ Show Material materials with Densidad of 1.52 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 3.1 % Show Material materials with Elongación of 3.1 % | ASTM D 638 | Type I, 5 mm/min |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 128 J/m Show Material materials with Impact strength, Izod notched, ASTM of 128 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 857 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 857 J/m | ASTM D 4812 |
Módulo de flexión | 23.0 °C | 7.81 GPa Show Material materials with Módulo de flexión of 7.81 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 8.66 GPa Show Material materials with Módulo elástico of 8.66 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 174 MPa Show Material materials with Resistencia a la flexión of 174 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 106 MPa Show Material materials with Resistencia a la tracción of 106 MPa | ASTM D 638 | Type I, 5 mm/min |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 208 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 1 V Show Material materials with Índice de seguimiento comparativo of 1 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción of 0.5 - 0.8 % | SABIC method | 3.2-4.6 mm |
Contracción transversal | 23.0 °C | 0.6 - 0.9 % Show Material materials with Contracción transversal of 0.6 - 0.9 % | SABIC method | 3.2-4.6 mm |
Velocidad de flujo de la masa derretida | 11.7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 11.7 g/10min | ASTM D 1238 | 250°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Circuit Protection,Data Management,Data Transfer,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,Food Processor,Gas/Electric Oven,Medical Device,Power Manangement,Recreational Vehicle,Water Treatment/Filtration,Wireless Communications,Wiring Devices,Wire & cable | |
| Fillers | 33% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |