Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Material materials with Elongación of 2 % | ISO 527 | 5 mm/min |
Hardness, Ball Indentation | 23.0 °C | 122 MPa Show Material materials with Hardness, Ball Indentation of 122 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 8 GPa Show Material materials with Módulo de flexión of 8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 9 GPa Show Material materials with Módulo elástico of 9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 170 MPa Show Material materials with Resistencia a la flexión of 170 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 115 MPa Show Material materials with Resistencia a la tracción of 115 MPa | ISO 527 | 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 40 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 40 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 45 kJ/m² | ISO 180/1U | |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-2 | -23°C to 80°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.05E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.05E-4 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature, 1.80 MPa | 160 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO 75/Ae | 1.8 MPa | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |||
Relative temperature index, mechanical impact | 110 °C Show Material materials with Relative temperature index, mechanical impact of 110 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 175 °C Show Material materials with Temperatura de reblandecimiento Vicat of 175 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating 2nd value | 3mm | UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.3 [-] Show Material materials with Constante dieléctrica of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 16 kV/mm Show Material materials with Rigidez dieléctrica of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 250 V Show Material materials with Índice de seguimiento comparativo of 250 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.6 % Show Material materials with Contracción of 0.4 - 0.6 % | SABIC method |
Contracción transversal | 23.0 °C | 0.5 - 0.9 % Show Material materials with Contracción transversal of 0.5 - 0.9 % | SABIC method |
Velocidad de flujo del volumen derretido | 8 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 8 cm³/10min | ISO 1133 | 250°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket,Building Accessory,Circuit Protection,Data Management,Data Transfer,Displays,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,EV Infrastructure,Forward Lighting,Gas/Electric Oven,Heavy Vehicles,Industrial Material Handling,Infotainment/Telematic,Interior,Lawn/Garden,LED Lighting,Medical Device,Meter Gas,Motorcycle,Personal Care,Photo/Video Camera,Washing Machine,Wireless Communications | |
Fillers | 30% Glass Fiber | |
Processing methods | Drying Temperature: 110-120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 240-260°C, Front - Zone 3 Temperature: 245-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Hopper Temperature: 40-60°C, Mold Temperature: 40-100°C |