General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 0.9 g/cm³ Show Material materials with Densidad of 0.9 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 57 [-] Show Material materials with Dureza Shore D of 57 [-] | ISO 868 |
Elongación | 23.0 °C | 160 % Show Material materials with Elongación of 160 % | ISO 527 | 50 mm/min |
Elongation at yield | 23.0 °C | 5.5 % Show Material materials with Elongation at yield of 5.5 % | ISO 527 | 50 mm/min |
Límite elástico | 23.0 °C | 18 MPa Show Material materials with Límite elástico of 18 MPa | ISO 527 | 50 mm/min |
Módulo de flexión | 23.0 °C | 0.89 GPa Show Material materials with Módulo de flexión of 0.89 GPa | ISO 178 | 2 mm/min, 64mm |
Módulo elástico | 23.0 °C | 0.85 GPa Show Material materials with Módulo elástico of 0.85 GPa | ISO 527 | 1 mm/min |
Resistencia a la tracción | 23.0 °C | 13 MPa Show Material materials with Resistencia a la tracción of 13 MPa | ISO 527 | 50 mm/min, 1A |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 59 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 59 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A |
23.0 °C | 49 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 49 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | -30.0 °C | 1.29E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.29E-4 1/K | ISO 11359-2 |
Coeficiente de dilatación térmica transversal | -30.0 °C | 1.48E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.48E-4 1/K | ISO 11359-2 |
Heat deflection temperature, 1.80 MPa | 51 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 51 °C | ISO 75-1&2 | 1.8 MPa | |
Temperatura de reblandecimiento Vicat | 136 °C Show Material materials with Temperatura de reblandecimiento Vicat of 136 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
Property | Value | Comment |
---|---|---|
Velocidad de flujo de la masa derretida | 19 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 19 g/10min | ISO 1133 | 230°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | The weatherable product was originally designed for unpainted automotive exterior bumper cap and step pad applications where high flexibility is required. | |
Fillers | Mineral Powder | |
Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa |