Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.02 g/cm³ Show Material materials with Densidad of 1.02 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Shore D | 23.0 °C | 66 [-] Show Material materials with Dureza Shore D of 66 [-] | ISO 868 |
Elongación | 23.0 °C | 22 % Show Material materials with Elongación of 22 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 45 J/m Show Material materials with Impact strength, Izod notched, ASTM of 45 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1080 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1080 J/m | ASTM D 4812 | 23°C, 63.5*12.7*3.2mm, Cut |
Límite elástico | 23.0 °C | 27 MPa Show Material materials with Límite elástico of 27 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.22 GPa Show Material materials with Módulo de flexión of 2.22 GPa | ISO 178 | 2 mm/min, 64mm |
Módulo elástico | 23.0 °C | 2.78 GPa Show Material materials with Módulo elástico of 2.78 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 20 MPa Show Material materials with Resistencia a la tracción of 20 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 2 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 2 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A |
23.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-6 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-6 1/K | ISO 11359-2 | -30°C to 100°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-5 1/K | ISO 11359-2 | -30°C to 100°C |
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ASTM D 648 | 1.82 MPa, 3.2 mm | |
Temperatura de reblandecimiento Vicat | 144 °C Show Material materials with Temperatura de reblandecimiento Vicat of 144 °C | ISO 306 | 10N, 50°C/hr |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1 % Show Material materials with Contracción of 1 % | SABIC method | 1 Hour, 80°C |
Contracción transversal | 23.0 °C | 1.4 % Show Material materials with Contracción transversal of 1.4 % | SABIC method | 1 Hour, 80°C |
Velocidad de flujo de la masa derretida | 21 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 21 g/10min | ISO 1133 | 230°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Overhead | |
| Fillers | Mineral Powder | |
| Processing methods | Drying Temperature: 80-100°C, Drying Time: 2-4hrs, Melt Temperature: 210-270°C, Nozzle Temperature: 210-270°C, Front - Zone 3 Temperature: 210-270°C, Middle - Zone 2 Temperature: 200-250°C, Rear - Zone 1 Temperature: 190-230°C, Mold Temperature: 15-60°C, Back Pressure: 1-1.5MPa | |