General
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 18 % Show Material materials with Elongación of 18 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 90 MPa Show Material materials with Flexural yield strength of 90 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 105 MPa Show Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 25 J/m Show Material materials with Impact strength, Izod notched, ASTM of 25 J/m | ASTM D 256 | ||
23.0 °C | 40 J/m Show Material materials with Impact strength, Izod notched, ASTM of 40 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 58 MPa Show Material materials with Límite elástico of 58 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.6 GPa Show Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.82 GPa Show Material materials with Módulo elástico of 2.82 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 52 MPa Show Material materials with Resistencia a la tracción of 52 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/2C | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/2C | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A | ||
23.0 °C | 5 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | |||
Impact strength, Izod unnotched, ASTM | No break @ 23,-30°C | ASTM D 4812 | ||||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.31E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.31E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.92E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7.92E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.24 W/(m·K) Show Material materials with Conductividad térmica of 0.24 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 71 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 71 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 170 °C Show Material materials with Temperatura de reblandecimiento Vicat of 170 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating | 3mm | UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 3 [-] Show Material materials with Constante dieléctrica of 3 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 18 kV/mm Show Material materials with Rigidez dieléctrica of 18 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 175 V Show Material materials with Índice de seguimiento comparativo of 175 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.5 - 2.3 % Show Material materials with Contracción of 1.5 - 2.3 % | SABIC method | 2.3-4.6 mm |
Contracción transversal | 23.0 °C | 1.6 - 2.4 % Show Material materials with Contracción transversal of 1.6 - 2.4 % | SABIC method | 2.3-4.6 mm |
Melt viscosity | 260.0 °C | 260 Pa·s Show Material materials with Melt viscosity of 260 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Velocidad de flujo de la masa derretida | 33 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 33 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Velocidad de flujo del volumen derretido | 30 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 30 cm³/10min | ISO 1133 | 265°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Building Accessory,Circuit Protection,Coffee Maker/Espresso Machine,Cooking Range,Data Management,Data Transfer,Dishwasher,Displays,Document Handling,Doors Hardware/Trim,Electronic components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Freezer,Furnace/Heater,Gas/Electric Oven,Hygiene/Personal Care,Industrial Material Handling,Lab Ware and Clinical Diagnostics,LED Lighting,Medical Device,Meter Gas,Microwave Oven,Motorcycle,Non-LED Lighting,Personal Care,Personal Computing,Photovoltaic Components,Power Manangement,Respiratory,Semiconductor,Small Appliance,Washing Machine,Water Treatment/Filtration,Wireless Communications,Wiring Devices,Wire & cable | |
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Nozzle Temperature: 240-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.025mm |