General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Material materials with Absorción de agua of 0.08 % | ASTM D 570 | 24 Hours |
Densidad | 23.0 °C | 1.34 g/cm³ Show Material materials with Densidad of 1.34 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 110 % Show Material materials with Elongación of 110 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5.28 % Show Material materials with Elongation at yield of 5.28 % | ASTM D 638 | 50 mm/min |
Flexural yield strength | 23.0 °C | 82 MPa Show Material materials with Flexural yield strength of 82 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Material materials with Hardness, Rockwell R of 117 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 534 J/m Show Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 |
Límite elástico | 23.0 °C | 48 MPa Show Material materials with Límite elástico of 48 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.06 GPa Show Material materials with Módulo de flexión of 2.06 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.05 GPa Show Material materials with Módulo elástico of 2.05 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la flexión | 23.0 °C | 82 MPa Show Material materials with Resistencia a la flexión of 82 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 48 MPa Show Material materials with Resistencia a la tracción of 48 MPa | ASTM D 638 | Type I, 50 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.24E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.24E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Heat deflection temperature, 1.80 MPa | 98 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 98 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating | 3mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.2 [-] Show Material materials with Constante dieléctrica of 3.2 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.03 [-] Show Material materials with Factor de disipación of 0.03 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 18.5 kV/mm Show Material materials with Rigidez dieléctrica of 18.5 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 2 V Show Material materials with Índice de seguimiento comparativo of 2 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1 - 1.4 % Show Material materials with Contracción of 1 - 1.4 % | SABIC method | 2.3-4.6 mm |
Contracción transversal | 23.0 °C | 1.2 - 1.6 % Show Material materials with Contracción transversal of 1.2 - 1.6 % | SABIC method | 2.3-4.6 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Conditioning,Air Filtration,Amusement Machine,Audio,Building Accessory,Commercial Storage/Cookware,Cooking Range,Data Transfer,Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Fluid Delivery,Freezer,Furnace/Heater,Heavy Vehicles,Industrial Material Handling,Lab Ware and Clinical Diagnostics,Lawn/Garden,LED Lighting,Medical Device,Medical Facility Infrastructure,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Photovoltaic Components,Plumbing,Power Manangement,Refrigerator,Renal and Blood Handling,Small Appliance,Surgical Devices,Swimming Pool/Spa,Traffic Management,Wearables,Window,Wireless Communications,Wiring Devices,Wire & cable | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |