General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.13 % Show Material materials with Absorción de agua of 0.13 % | ISO 62 | 23°C, 50% RH |
Absorción de agua, equilibrio | 23.0 °C | 0.31 % Show Material materials with Absorción de agua, equilibrio of 0.31 % | ASTM D 570 |
Densidad | 23.0 °C | 1.26 g/cm³ Show Material materials with Densidad of 1.26 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Rockwell M | 23.0 °C | 85 [-] Show Material materials with Dureza Rockwell M of 85 [-] | ASTM D 785 | ||
Elongación | 23.0 °C | 12 % Show Material materials with Elongación of 12 % | ASTM D 638 | Type I, 5 mm/min | ||
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 95 MPa Show Material materials with Flexural yield strength of 95 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 115 MPa Show Material materials with Hardness, Ball Indentation of 115 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Material materials with Hardness, Rockwell R of 124 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 80 J/m Show Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | ||
23.0 °C | 107 J/m Show Material materials with Impact strength, Izod notched, ASTM of 107 J/m | ASTM D 256 | |||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 | ||
Límite elástico | 23.0 °C | 63 MPa Show Material materials with Límite elástico of 63 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Módulo de flexión | 23.0 °C | 3.4 GPa Show Material materials with Módulo de flexión of 3.4 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 3.93 GPa Show Material materials with Módulo elástico of 3.93 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la flexión | 23.0 °C | 108 MPa Show Material materials with Resistencia a la flexión of 108 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Resistencia a la tracción | 23.0 °C | 48 MPa Show Material materials with Resistencia a la tracción of 48 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 15 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 15 kJ/m² | ISO 179/2C | ||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | ||
23.0 °C | 8 - 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 - 10 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 130 kJ/m² | ISO 180/1U | ||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Calor específico | 23.0 °C | 1210 J/(kg·K) Show Material materials with Calor específico of 1210 J/(kg·K) | ASTM C 351 | ||
Coeficiente de dilatación térmica | 23.0 °C | 4.68E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4.68E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.46E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8.46E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.21 W/(m·K) Show Material materials with Conductividad térmica of 0.21 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 138 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 138 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 149 °C Show Material materials with Temperatura de reblandecimiento Vicat of 149 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Compliant, 94-5VB Rating | 2mm | UL 94 by SABIC-IP |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.9 [-] Show Material materials with Constante dieléctrica of 2.9 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 16 kV/mm Show Material materials with Rigidez dieléctrica of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 175 V Show Material materials with Índice de seguimiento comparativo of 175 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 7 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 7 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Circuit Protection,Data Transfer,Displays,Document Handling,Electronic Components,Enclosures,Energy Management,Lab Ware and Clinical Diagnostics,Travel Suitcase,Wiring Devices,Wire & cable | |
Fillers | 10% Glass Fiber | |
Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C |