Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.13 % Show Material materials with Absorción de agua of 0.13 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.26 g/cm³ Show Material materials with Densidad of 1.26 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Rockwell M | 23.0 °C | 85 [-] Show Material materials with Dureza Rockwell M of 85 [-] | ASTM D 785 | ||
Elongación | 23.0 °C | 12 % Show Material materials with Elongación of 12 % | ASTM D 638 | Type I, 5 mm/min | ||
Elongation at yield | 23.0 °C | 3 % Show Material materials with Elongation at yield of 3 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 108 MPa Show Material materials with Flexural yield strength of 108 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Hardness, Rockwell R | 23.0 °C | 124 [-] Show Material materials with Hardness, Rockwell R of 124 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 106 J/m Show Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 | ||
Límite elástico | 23.0 °C | 63 MPa Show Material materials with Límite elástico of 63 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Módulo de flexión | 23.0 °C | 3.52 GPa Show Material materials with Módulo de flexión of 3.52 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span | ||
Módulo elástico | 23.0 °C | 3.93 GPa Show Material materials with Módulo elástico of 3.93 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 48 MPa Show Material materials with Resistencia a la tracción of 48 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | ||
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 130 kJ/m² | ISO 179/1eU | ||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | ||
23.0 °C | 10 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 130 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 130 kJ/m² | ISO 180/1U | ||
Impact strength, Izod unnotched, ASTM | No break @ 23°C | ASTM D 4812 | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Calor específico | 23.0 °C | 1210 J/(kg·K) Show Material materials with Calor específico of 1210 J/(kg·K) | ASTM C 351 | ||
Coeficiente de dilatación térmica | 23.0 °C | 4.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4.7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 | ||
Heat deflection temperature, 0.45 MPa | 140 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 140 °C | ISO 75/Bf | 0.45 MPa | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 143 °C Show Material materials with Temperatura de reblandecimiento Vicat of 143 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Resistividad eléctrica | 23.0 °C | 1.00E+13 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+13 Ω·m | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 175 V Show Material materials with Índice de seguimiento comparativo of 175 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.3 % Show Material materials with Contracción of 0.3 % | SABIC method | 3.2 mm |
Velocidad de flujo del volumen derretido | 9 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 9 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Energy Management | |
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |