General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.07 % Show Material materials with Absorción de agua of 0.07 % | ASTM D 570 | 24 Hours |
Densidad | 23.0 °C | 1.58 g/cm³ Show Material materials with Densidad of 1.58 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 640 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 640 J/m | ASTM D 4812 |
Módulo de flexión | 23.0 °C | 6.89 GPa Show Material materials with Módulo de flexión of 6.89 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la flexión | 23.0 °C | 179 MPa Show Material materials with Resistencia a la flexión of 179 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 110 MPa Show Material materials with Resistencia a la tracción of 110 MPa | ASTM D 638 | Type I, 5 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.16E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.16E-5 1/K | ASTM E 831 | 60°C to 138°C | ||
Heat deflection temperature, 1.80 MPa | 160 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | |||
Relative temperature index, mechanical impact | 110 °C Show Material materials with Relative temperature index, mechanical impact of 110 °C | UL 746B | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | |||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating | 2.31mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.7 [-] Show Material materials with Constante dieléctrica of 3.7 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | ASTM D 150 | at 1 MHz |
Resistividad eléctrica | 23.0 °C | 4.30E+14 Ω·m Show Material materials with Resistividad eléctrica of 4.30E+14 Ω·m | ASTM D 257 |
Rigidez dieléctrica | 23.0 °C | 25.5 kV/mm Show Material materials with Rigidez dieléctrica of 25.5 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.8 % Show Material materials with Contracción of 0.5 - 0.8 % | SABIC method | 3.2-4.6 mm |
Contracción transversal | 23.0 °C | 0.6 - 0.9 % Show Material materials with Contracción transversal of 0.6 - 0.9 % | SABIC method | 3.2-4.6 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Building Accessory,Data Transfer,Document Handling,Electronic Components,Enclosures,Meter Water,Non-LED Lighting,Oil/Gas,Photovoltaic Components,Recreational Vehicle,Small Appliance,Water Treatment/Filtration,Weaving Machine | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-265°C, Nozzle Temperature: 245-260°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 245-260°C, Rear - Zone 1 Temperature: 240-255°C, Mold Temperature: 65-90°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.025-0.038mm | |