Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 145 % Show Material materials with Elongación of 145 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 4.2 % Show Material materials with Elongation at yield of 4.2 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 60 MPa Show Material materials with Flexural yield strength of 60 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | -30.0 °C | 667 J/m Show Material materials with Impact strength, Izod notched, ASTM of 667 J/m | ASTM D 256 |
23.0 °C | 897 J/m Show Material materials with Impact strength, Izod notched, ASTM of 897 J/m | ASTM D 256 | |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 |
Límite elástico | 23.0 °C | 43 MPa Show Material materials with Límite elástico of 43 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 1.69 GPa Show Material materials with Módulo de flexión of 1.69 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 1.78 GPa Show Material materials with Módulo elástico of 1.78 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 32 MPa Show Material materials with Resistencia a la tracción of 32 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 72 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 72 kJ/m² | ISO 179/1eA |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 51 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 51 kJ/m² | ISO 180/1A |
23.0 °C | 54 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 54 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.89E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9.89E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.05E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.05E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 60 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 60 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 123 °C Show Material materials with Temperatura de reblandecimiento Vicat of 123 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Material materials with Índice de seguimiento comparativo of 0 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.6 - 1.8 % Show Material materials with Contracción of 1.6 - 1.8 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1.6 - 1.8 % Show Material materials with Contracción transversal of 1.6 - 1.8 % | SABIC method |
Velocidad de flujo de la masa derretida | 21.9 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 21.9 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Velocidad de flujo del volumen derretido | 17 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 17 cm³/10min | ISO 1133 | 265°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Audio,Building Accessory,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior,Industrial Material Handling,Medical Facility Infrastructure,Monitoring and Imaging,Personal Computing,Recreational Vehicle,Security/Detection,Irrigation | |
| Processing methods | Drying Temperature: 105-115°C, Drying Time: 2-4hrs, Drying Time (Cumulative): 6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 250-270°C, Front - Zone 3 Temperature: 250-265°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-245°C, Mold Temperature: 40-80°C, Back Pressure: 0.2-0.3MPa, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |