Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.15 % Show Material materials with Absorción de agua of 0.15 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.23 g/cm³ Show Material materials with Densidad of 1.23 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 4 % Show Material materials with Elongación of 4 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 3.5 % Show Material materials with Elongation at yield of 3.5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 150 MPa Show Material materials with Flexural yield strength of 150 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 78 J/m Show Material materials with Impact strength, Izod notched, ASTM of 78 J/m | ASTM D 256 |
Límite elástico | 23.0 °C | 92 MPa Show Material materials with Límite elástico of 92 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 4.28 GPa Show Material materials with Módulo de flexión of 4.28 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 5.33 GPa Show Material materials with Módulo elástico of 5.33 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 91 MPa Show Material materials with Resistencia a la tracción of 91 MPa | ASTM D 638 | Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/2C |
23.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/2C | |
Resistencia al choque, ensayo Charpy no entallado | -30.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 100 kJ/m² | ISO 179/1eU | |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | -30.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 80 kJ/m² | ISO 180/1U |
23.0 °C | 80 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 80 kJ/m² | ISO 180/1U | |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 4E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 4E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 4E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature, 1.80 MPa | 141 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 141 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 148 °C Show Material materials with Temperatura de reblandecimiento Vicat of 148 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 1.5mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.2 [-] Show Material materials with Constante dieléctrica of 3.2 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.01 [-] Show Material materials with Factor de disipación of 0.01 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 20 kV/mm Show Material materials with Rigidez dieléctrica of 20 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Índice de seguimiento comparativo | 23.0 °C | 150 V Show Material materials with Índice de seguimiento comparativo of 150 V | IEC 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.2 - 0.5 % Show Material materials with Contracción of 0.2 - 0.5 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.2 - 0.5 % Show Material materials with Contracción transversal of 0.2 - 0.5 % | SABIC method |
Velocidad de flujo de la masa derretida | 6.5 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6.5 g/10min | ASTM D 1238 | 300°C/1.2 kg | |
Velocidad de flujo del volumen derretido | 6 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 6 cm³/10min | ISO 1133 | 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Displays,Document Handling,Electronic Components,LED Lighting,Personal Computing,Plumbing,Wireless Communications | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Temperature: 120°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 290-320°C, Nozzle Temperature: 280-310°C, Front - Zone 3 Temperature: 290-320°C, Middle - Zone 2 Temperature: 280-310°C, Rear - Zone 1 Temperature: 270-300°C, Hopper Temperature: 60-80°C, Mold Temperature: 80-120°C | |