General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Material materials with Elongación of 2.5 % | ISO 527 | 5 mm/min |
Elongation at yield | 23.0 °C | 2.5 % Show Material materials with Elongation at yield of 2.5 % | ISO 527 | 5 mm/min |
Hardness, Ball Indentation | 23.0 °C | 116 MPa Show Material materials with Hardness, Ball Indentation of 116 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Límite elástico | 23.0 °C | 90 MPa Show Material materials with Límite elástico of 90 MPa | ISO 527 | 5 mm/min |
Módulo de flexión | 23.0 °C | 5.3 GPa Show Material materials with Módulo de flexión of 5.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 6 GPa Show Material materials with Módulo elástico of 6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 135 MPa Show Material materials with Resistencia a la flexión of 135 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 90 MPa Show Material materials with Resistencia a la tracción of 90 MPa | ISO 527 | 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 8 - 9 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 8 - 9 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 15 - 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy no entallado of 15 - 30 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A |
23.0 °C | 8 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 15 - 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 15 - 25 kJ/m² | ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Material materials with Conductividad térmica of 0.2 W/(m·K) | ISO 8302 |
Heat deflection temperature, 1.80 MPa | 129 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ISO 75/Ae | 1.8 MPa | |
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |
Temperatura de reblandecimiento Vicat | 137 °C Show Material materials with Temperatura de reblandecimiento Vicat of 137 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.2 - 0.4 % Show Material materials with Contracción of 0.2 - 0.4 % | SABIC method |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Air Filtration,Data Management,Electronic Components,Enclosure/Housing/Cover,Enclosures,Lab Ware and Clinical Diagnostics,Personal Computing,Small Appliance,Structure,Wireless Communications | |
Fillers | 20% Glass Fiber | |
Processing methods | Drying Temperature: 100-110°C, Drying Time: 2-4hrs, Melt Temperature: 240-280°C, Mold Temperature: 50-80°C |