General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.15 % Show Material materials with Absorción de agua of 0.15 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.22 g/cm³ Show Material materials with Densidad of 1.22 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 50 % Show Material materials with Elongación of 50 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 82 MPa Show Material materials with Hardness, Ball Indentation of 82 MPa | ISO 2039-1 | ||
Hardness, Rockwell L | 23.0 °C | 89 [-] Show Material materials with Hardness, Rockwell L of 89 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m | ASTM D 256 | ||
23.0 °C | 625 J/m Show Material materials with Impact strength, Izod notched, ASTM of 625 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 53 MPa Show Material materials with Límite elástico of 53 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2 GPa Show Material materials with Módulo de flexión of 2 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.05 GPa Show Material materials with Módulo elástico of 2.05 GPa | ASTM D 638 | 50 mm/min | ||
Resistencia a la tracción | 23.0 °C | 49 MPa Show Material materials with Resistencia a la tracción of 49 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/2C | ||
-20.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | ISO 179/2C | |||
23.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | ISO 179/2C | |||
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 25 kJ/m² | ISO 180/1A | ||
-30.0 °C | 35 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 35 kJ/m² | ISO 180/1A | |||
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 50 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9.5E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.18 W/(m·K) Show Material materials with Conductividad térmica of 0.18 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 1.80 MPa | 83 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 83 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Temperatura de reblandecimiento Vicat | 120 °C Show Material materials with Temperatura de reblandecimiento Vicat of 120 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating | 1.5mm | UL 94 by SABIC-IP |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.3 [-] Show Material materials with Constante dieléctrica of 3.3 [-] | IEC 60250 | at 50/60 Hz |
Factor de disipación | 23.0 °C | 0.02 [-] Show Material materials with Factor de disipación of 0.02 [-] | IEC 60250 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.7 - 1.1 % Show Material materials with Contracción of 0.7 - 1.1 % | SABIC method |
Contracción transversal | 23.0 °C | 0.7 - 1.1 % Show Material materials with Contracción transversal of 0.7 - 1.1 % | SABIC method |
Velocidad de flujo de la masa derretida | 14 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 14 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 | 250°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Applique,Auto Aftermarket,Electronic Components,Exterior Trim,Heavy Vehicles,Laundry Dryer,Meter Gas,Recreational Vehicle | |
Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C |