General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua, equilibrio | 23.0 °C | 0.55 % Show Material materials with Absorción de agua, equilibrio of 0.55 % | ASTM D 570 |
Densidad | 23.0 °C | 1.06 g/cm³ Show Material materials with Densidad of 1.06 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 40 % Show Material materials with Elongación of 40 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 58 MPa Show Material materials with Flexural yield strength of 58 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Hardness, Rockwell R | 23.0 °C | 86 [-] Show Material materials with Hardness, Rockwell R of 86 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | -30.0 °C | 58 J/m Show Material materials with Impact strength, Izod notched, ASTM of 58 J/m | ASTM D 256 |
23.0 °C | 320 J/m Show Material materials with Impact strength, Izod notched, ASTM of 320 J/m | ASTM D 256 | |
Límite elástico | 23.0 °C | 41 MPa Show Material materials with Límite elástico of 41 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 1.79 GPa Show Material materials with Módulo de flexión of 1.79 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 1.79 GPa Show Material materials with Módulo elástico of 1.79 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 34 MPa Show Material materials with Resistencia a la tracción of 34 MPa | ASTM D 638 | Type I, 50 mm/min |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ASTM E 831 | 0°C to 100°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.18E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 9.18E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 79 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 79 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 99 °C Show Material materials with Temperatura de reblandecimiento Vicat of 99 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating | 1.47mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.21 [-] Show Material materials with Constante dieléctrica of 3.21 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 0.03 [-] Show Material materials with Factor de disipación of 0.03 [-] | ASTM D 150 | at 1 MHz |
Rigidez dieléctrica | 23.0 °C | 15.9 kV/mm Show Material materials with Rigidez dieléctrica of 15.9 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Material materials with Índice de seguimiento comparativo of 0 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 13 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 13 g/10min | ASTM D 1238 | 260°C/5.0 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Document Handling,Electronic Components,Enclosure/Housing/Cover,Enclosures,Exterior Mirror,Exterior Trim,Front Grille,Heavy Vehicles,LED Lighting,Medical Device,Medical Facility Infrastructure,Meter Water,Personal Computing,Power Boat,Respiratory,Surgical Devices,Swimming Pool/Spa,Wireless Communications,Wiring Devices | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 3-6hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 240-270°C, Nozzle Temperature: 240-270°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 225-260°C, Rear - Zone 1 Temperature: 220-250°C, Mold Temperature: 55-75°C, Back Pressure: 0.7-1.4MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm | |