| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 99 % Show Material materials with Elongación of 99 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 450 J/m Show Material materials with Impact strength, Izod notched, ASTM of 450 J/m | ASTM D 256 |
Límite elástico | 23.0 °C | 56 MPa Show Material materials with Límite elástico of 56 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.88 GPa Show Material materials with Módulo de flexión of 2.88 GPa | ISO 178 | 2 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 11 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 83 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ISO 75/Bf | 0.45 MPa | |||
Relative temperature index, electrical | 60 °C Show Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Inflamabilidad | UL Compliant, 94-5VB Rating | 1.5mm | UL 94 by SABIC-IP | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+17 Ω·cm Show Material materials with Volume resistivity of 1.00E+17 Ω·cm | ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Material materials with Índice de seguimiento comparativo of 0 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.23 % Show Material materials with Contracción of 0.23 % | SABIC method | 1.5-3.2 mm |
Contracción transversal | 23.0 °C | 0.31 % Show Material materials with Contracción transversal of 0.31 % | SABIC method | 1.5-3.2 mm |
Velocidad de flujo de la masa derretida | 27 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 27 g/10min | ASTM D 1238 | 260°C/2.16 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Displays,Document Handling | |
| Processing methods | Drying Temperature: 80-90°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 245-275°C, Nozzle Temperature: 245-275°C, Front - Zone 3 Temperature: 245-275°C, Middle - Zone 2 Temperature: 220-265°C, Rear - Zone 1 Temperature: 220-255°C, Mold Temperature: 60-80°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |