Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.1 % Show Material materials with Absorción de agua of 0.1 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.18 g/cm³ Show Material materials with Densidad of 1.18 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 85 % Show Material materials with Elongación of 85 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 6 % Show Material materials with Elongation at yield of 6 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 96 MPa Show Material materials with Flexural yield strength of 96 MPa | ISO 178 | 2 mm/min | ||
Límite elástico | 23.0 °C | 64 MPa Show Material materials with Límite elástico of 64 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.47 GPa Show Material materials with Módulo de flexión of 2.47 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.33 GPa Show Material materials with Módulo elástico of 2.33 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 62 MPa Show Material materials with Resistencia a la tracción of 62 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 20 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | ||
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 50 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 95 °C Show Material materials with Relative temperature index, mechanical impact of 95 °C | UL 746B | |||
Relative temperature index, mechanical strength | 100 °C Show Material materials with Relative temperature index, mechanical strength of 100 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 134 °C Show Material materials with Temperatura de reblandecimiento Vicat of 134 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94-5VB Flame Class Rating | 2.5mm | UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica | 23.0 °C | 2.95 [-] Show Material materials with Constante dieléctrica of 2.95 [-] | ASTM D 150 | at 1 MHz |
Factor de disipación | 23.0 °C | 8.8E-3 [-] Show Material materials with Factor de disipación of 8.8E-3 [-] | ASTM D 150 | at 1 MHz |
Resistividad eléctrica | 23.0 °C | 1.00E+13 Ω·m Show Material materials with Resistividad eléctrica of 1.00E+13 Ω·m | IEC 60093 |
Surface resistivity | 23.0 °C | 4.00E+16 Ω/sq Show Material materials with Surface resistivity of 4.00E+16 Ω/sq | IEC 60093 | ROA |
Índice de seguimiento comparativo | 23.0 °C | 3 V Show Material materials with Índice de seguimiento comparativo of 3 V | UL 746A |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 - 0.8 % Show Material materials with Contracción of 0.4 - 0.8 % | SABIC method | 3.2 mm |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 | 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Circuit Protection,Cooking Range,Data Transfer,Displays,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,LED Lighting,Medical Device,Microwave Oven,Monitoring and Imaging,Non-LED Lighting,Personal Computing,Photovoltaic Components,Power Manangement,Refrigerator,Small Appliance,Wireless Communications | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-300°C, Nozzle Temperature: 230-290°C, Front - Zone 3 Temperature: 240-300°C, Middle - Zone 2 Temperature: 230-290°C, Rear - Zone 1 Temperature: 210-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |