Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Material materials with Absorción de agua of 0.2 % | ISO 62 | 23°C, 50% RH |
Densidad | 23.0 °C | 1.12 g/cm³ Show Material materials with Densidad of 1.12 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 75 % Show Material materials with Elongación of 75 % | ASTM D 638 | Type I, 50 mm/min | ||
Elongation at yield | 23.0 °C | 5.3 % Show Material materials with Elongation at yield of 5.3 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 85 MPa Show Material materials with Flexural yield strength of 85 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 300 J/m Show Material materials with Impact strength, Izod notched, ASTM of 300 J/m | ASTM D 256 | ||
23.0 °C | 600 J/m Show Material materials with Impact strength, Izod notched, ASTM of 600 J/m | ASTM D 256 | |||
Límite elástico | 23.0 °C | 58 MPa Show Material materials with Límite elástico of 58 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Módulo de flexión | 23.0 °C | 2.3 GPa Show Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.25 GPa Show Material materials with Módulo elástico of 2.25 GPa | ASTM D 638 | 5 mm/min | ||
Resistencia a la tracción | 23.0 °C | 50 MPa Show Material materials with Resistencia a la tracción of 50 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 25 kJ/m² | ISO 179/1eA | ||
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 50 kJ/m² | ISO 179/1eA | |||
Resistencia al choque, ensayo Izod entallado | -30.0 °C | 25 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 25 kJ/m² | ISO 180/1A | ||
23.0 °C | 50 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 50 kJ/m² | ISO 180/1A | |||
Resistencia al choque, ensayo Charpy no entallado | No Break @ 23,-30°C | ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | No Break @ 23,-30°C| ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Temperatura de reblandecimiento Vicat | 131 °C Show Material materials with Temperatura de reblandecimiento Vicat of 131 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Contracción transversal of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |