Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.11 g/cm³ Show Material materials with Densidad of 1.11 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 70 % Show Material materials with Elongación of 70 % | ASTM D 638 | Type I, 5 mm/min |
Elongation at yield | 23.0 °C | 3.9 % Show Material materials with Elongation at yield of 3.9 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 75 MPa Show Material materials with Flexural yield strength of 75 MPa | ISO 178 | 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 500 - 620 J/m Show Material materials with Impact strength, Izod notched, ASTM of 500 - 620 J/m | ASTM D 256 |
Límite elástico | 23.0 °C | 47 MPa Show Material materials with Límite elástico of 47 MPa | ASTM D 638 | Type I, 5 mm/min |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Material materials with Módulo de flexión of 2.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.33 GPa Show Material materials with Módulo elástico of 2.33 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la tracción | 23.0 °C | 40 MPa Show Material materials with Resistencia a la tracción of 40 MPa | ISO 527 | 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 30 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | ISO 179/1eA |
23.0 °C | 65 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 65 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod entallado | -40.0 °C | 21 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 21 kJ/m² | ISO 180/1A |
23.0 °C | 56 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod entallado of 56 kJ/m² | ISO 180/1A | |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 101 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 101 °C | ASTM D 648 | 1.82 MPa, 6.4 mm, unannealed |
Temperatura de reblandecimiento Vicat | 114 °C Show Material materials with Temperatura de reblandecimiento Vicat of 114 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Velocidad de flujo de la masa derretida | 9 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 9 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Forward Lighting,Golf Cart,Medical Device,Motorcycle | |
| Processing methods | Drying Temperature: 100-105°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 260-290°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 255-290°C, Middle - Zone 2 Temperature: 255-290°C, Rear - Zone 1 Temperature: 250-280°C, Mold Temperature: 75-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm | |