General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.44 g/cm³ Show Material materials with Densidad of 1.44 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 18 % Show Material materials with Elongación of 18 % | ASTM D 638 | Type I, 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 |
Límite elástico | 23.0 °C | 60 MPa Show Material materials with Límite elástico of 60 MPa | ASTM D 638 | Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.68 GPa Show Material materials with Módulo de flexión of 2.68 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.13 GPa Show Material materials with Módulo elástico of 2.13 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la tracción | 23.0 °C | 23 MPa Show Material materials with Resistencia a la tracción of 23 MPa | ASTM D 638 | Type I, 50 mm/min |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.53E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 1.53E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.75E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.75E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 53 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 53 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Temperatura de reblandecimiento Vicat | 77 °C Show Material materials with Temperatura de reblandecimiento Vicat of 77 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating | 0.76mm | UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Material materials with Índice de seguimiento comparativo of 0 V | UL 746A |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 2 - 2.2 % Show Material materials with Contracción of 2 - 2.2 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 6.9 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 6.9 g/10min | ASTM D 1238 | 250°C/5.0 kgf |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Temperature: 120°C, Drying Time: 3-4hrs, Drying Time (Cumulative): 12hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 245-260°C, Nozzle Temperature: 240-255°C, Front - Zone 3 Temperature: 245-260°C, Middle - Zone 2 Temperature: 240-255°C, Rear - Zone 1 Temperature: 230-250°C, Mold Temperature: 50-75°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 50-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.025mm |